SABIC Innovative Plastics Lexan® EXL9330P PC COPOLYMER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EXL9330P PC COPOLYMER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Hardness, H358/30 90.0 MPa
13100 psi
ISO 2039-1
Tensile Strength at Break 60.0 MPa
8700 psi
50 mm/min; ISO 527
61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 125 %
125 %
50 mm/min; ISO 527
130 %
130 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.10 GPa
305 ksi
50 mm/min; ASTM D638
2.10 GPa
305 ksi
1 mm/min; ISO 527
Flexural Yield Strength 85.0 MPa
12300 psi
2 mm/min; ISO 178
88.0 MPa
12800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.06 GPa
299 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.20 GPa
319 ksi
2 mm/min; ISO 178
Izod Impact, Notched 8.01 J/cm
15.0 ft-lb/in
ASTM D256
10.68 J/cm
20.01 ft-lb/in
Izod Impact, double-gated, 23°C; SABIC Method
5.87 J/cm

@Temperature -50.0 °C
 11.0 ft-lb/in

@Temperature -58.0 °F
 ASTM D256
6.78 J/cm

@Temperature -30.0 °C
 12.7 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
6.41 J/cm

@Thickness 6.40 mm
 12.0 ft-lb/in

@Thickness 0.252 in
 ASTM D256
Izod Impact, Notched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
80*10*3; ISO 180/1A
55.0 kJ/m²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
65.0 kJ/m²

@Temperature -30.0 °C
 30.9 ft-lb/in²

@Temperature -22.0 °F
 63.5*12.7*3.2; ISO 180/4A
80.0 kJ/m²

@Temperature 23.0 °C
 38.1 ft-lb/in²

@Temperature 73.4 °F
 63.5*12.7*3.2; ISO 180/4A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 7.50 J/cm²
35.7 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
6.00 J/cm²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 52.0 J

@Temperature 23.0 °C
 38.4 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
72.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 40.0 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 66.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
 37.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
77.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 42.8 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 135 °C
275 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
134 °C

@Thickness 3.20 mm
 273 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 124 °C
255 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
120 °C

@Thickness 3.20 mm
 248 °F

@Thickness 0.126 in
 unannealed; ASTM D648
124 °C

@Thickness 6.40 mm
 255 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 140 °C
284 °F
Rate B/50; ISO 306
142 °C
288 °F
Rate B/120; ISO 306
142 °C
288 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 125 °C
257 °F
UL 746B
UL RTI, Mechanical with Impact 115 °C
239 °F
UL 746B
UL RTI, Mechanical without Impact 120 °C
248 °F
UL 746B
Flammability, UL94 V-1

@Thickness 0.800 mm
 V-1

@Thickness 0.0315 in
 UL 94
V-0

@Thickness 1.49 mm
 V-0

@Thickness 0.0587 in
 UL 94
5VA

@Thickness 2.99 mm
 5VA

@Thickness 0.118 in
 UL 94
Oxygen Index 35 %
35 %
ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
 406 kV/in

@Thickness 0.126 in
 in oil; IEC 60243-1
17.0 kV/mm

@Thickness 3.20 mm
 432 kV/in

@Thickness 0.126 in
 in oil; ASTM D149
Dissipation Factor 0.0010

@Frequency 50.0 - 60.0 Hz
 0.0010

@Frequency 50.0 - 60.0 Hz
 IEC 60250
0.0024

@Frequency 50.0 - 60.0 Hz
 0.0024

@Frequency 50.0 - 60.0 Hz
 ASTM D150
0.0085

@Frequency 1.00e+6 Hz
 0.0085

@Frequency 1.00e+6 Hz
 ASTM D150
0.0085

@Frequency 1.00e+6 Hz
 0.0085

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
225 V
225 V
IEC 60112
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A