- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 135 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 135 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Lexan® 920A PC (Europe-Africa-Middle East) LEXAN 920A is a medium viscosity flame retardant grade, especially suitable for electrical applications. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Polymer Resources PC-FD2-[color]-1 Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold Release, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, Medium Flow with Mold Release, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-p.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Polymer Resources PC-FR2A-D Polycarbonate, Flame Retardant, Medium Flow Polycarbonate, Flame Retardant, Medium FlowFeatures: • High Impact Resistance • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-i.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Polymer Resources PC-FR2-D Polycarbonate, Improved Flame Retardant, Medium Flow Polycarbonate, Improved Flame Retardant, Medium FlowFeatures: • High Impact Resistance • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | |
| Radici Radilon® S USX200 (dry) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Lexan® PC1800 PC (Asia Pacific) PC1800 resin is a medium-high flow (MFR = 18 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold rel.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Lubricomp DL002E PC (Europe-Africa-Middle East) LNP* Lubricomp* DL002E is a compound based on Polycarbonate resin containing PTFE. Added features include: Internally Lubricated, Easy Molding.This data was supplied by SABIC-IP for the Europe-Afric.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| SABIC Innovative Plastics Lexan® 925U PC (Europe-Africa-Middle East) Lexan* 925U Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is UV stabilized, providing additio.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| PTS Tristar® PC-10FR-(VIM) 12 MFI Flame Retardant, UV Stabilized Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics Lexan® VR2020 PC (Europe-Africa-Middle East) VR2020 resin is a medium-high flow (MFR = 18 at 300ºC/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 6.40 mm |
275 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOL HI5204B PP+MF20% Description: Injection Molding, PP+MF20%, Good WeatherabilityApplication: Automotive Interior PartsCAS: 9003-07-0 and 14807-96-6Information provided by LG Chemical |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | |
| LATI Latistat 87/28-06 PC Dissipative product based on Polycarbonate (PC). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DX07404H PC LNP* LUBRICOMP* DX07404H is a compound based on Polycarbonate containing Proprietary Fillers. Added features of this grade are: Healthcare, Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
ASTM D 648 |
| SABIC Innovative Plastics PC1800 PC (Europe-Africa-Middle East) PC1800 resin is a medium-high flow (MFR = 18 at 300ºC/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics PC1800R PC (Europe-Africa-Middle East) PC1800R resin is a medium-high flow (MFR = 18 at 300ºC/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was suppli.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics PC1803R PC (Asia Pacific) PC1803R resin is a medium-high flow (MFR = 18 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP STAT-KON DD000P PC LNP* STAT-KON* DD000P is a compound based on Polycarbonate resin containing Carbon. Added features of this material include: Electrically Conductive, Exceptional Processing. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| SPS Guang Zhou SAMATâ„¢ EP 5001(f1) Flame-retarded Polypropylene Characteristic: Good flame retardance, non-halogen, high flow properties, high rigidity, high heat resistance, meets the requirements of RoHs and PaHs, excellent UV resistanceApplications: X'mas dec.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GFN1 PPE+HIPS (Asia Pacific) PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including wate.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | DIN 53461 |
| Polyram RamTough PZ500 Polycarbonate, Flame Retardant Flame retardant polycarbonate for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Ecomass® 1050TU96 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting balancing and radiation shielding applicationsHigh Specific GravityTungsten Powder Filled Polyamide (PA) AlloyGood ToughnessInformation provided by Techn.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Ecomass® 1066ZD96 Tungsten Filled Polyamide Nontoxic alternative to Lead (Pb), weighting and balancing applicationsHigh Specific GravityTungsten Powder Filled Polyamide (PA) AlloyGood ToughnessInformation provided by Technical Polymers |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1,-2 |
| Covestro Makrolon® 2667 Polycarbonate Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Flame retardant• Med.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75 |
| Eurotec® Tecotek® PC44 GR10 GR003 ZG70 PC, 10% glass fiber reinforced, flame retardant - halogen (RoHS compliant), light grey Information provided by Eurotec® |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-2 |
| BASF Ultradur® B 6550 LN PBT Description: High-viscosity grades for the extrusion of loose buffer tubes for optical fibers, semi-finished products for machining, profiles and pipes.Information provided by BASF |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| A. Schulman POLYFORT™ FPP 1602 Glass Reinforced, Chemically Coupled Homopolymer DescriptionPolyfort® FPP 1602 is a 10% glass reinforced chemically coupled homopolymer.Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Asahi Kasei Xyron® A0501 PPE/PA AutomotiveInformation provided by Asahi Kasei |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DL002ER PC (Asia Pacific) LNP* Lubricomp* DL002ER is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated, Easy Molding, Mold Release. |
|||