- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 124 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 124 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
Ovation Polymers Nima™ NH PC151 Polycarbonate
Non-Hal FR-PC with High HDT, high impact and improved processability. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accordi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL1443T PC Copolymer
Lexan* EXL1443T polycarbonate (PC) siloxane copolymer resin is an injection molding grade with FDA and EU food contact compliance. This resin offers excellent low temperature (-30 C) ductility in co..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® EXL1444 PC Copolymer (Europe-Africa-Middle East)
Lexan* EXL1444 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade suitable for FDA compliant applications. This resin offers extreme low temperature (-..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL1463T PC Copolymer (Asia Pacific)
Lexan* EXL1463T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature (-30 C) ductility in combination with medium flow ch..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® EXL9112 PC Copolymer (Asia Pacific)
Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temp. ductility. Non-chlorinated, non-brominated flame retardant product. UL rated V-0/5VA.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® EXL9132 PC Copolymer
Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temperature ductility, UV stabilized. Non-chlorinated, non-brominated flame retardant product. UL rated V0/5VA.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® EXL9330P PC COPOLYMER (Asia Pacific)
Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
|
Ravago Manufacturing Americas Hylex® P1010LLT Polycarbonate
Information provided by Ravago.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® FXD923A PC (Europe-Africa-Middle East)
LEXAN FXD923A is a transparent/translucent, medium viscosity, flame retardent grade for light diffusion special effects. UV-stabilized. Color package may affect performance.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® FXE921A PC (Europe-Africa-Middle East)
LEXAN FXE921A is a transparent/translucent, medium viscosity, flame retardant grade with a fluorescent appearance. Color package may affect performance.This data was supplied by SABIC-IP for the Eur..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HP6NR PC (Europe-Africa-Middle East)
Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains no ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® HPS6 PC
Med/low flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO, steam e-beam and gamma sterilizable. ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® HPX4EU PC Copolymer (Europe-Africa-Middle East)
Medium flow specialty polycarbonate - improved processability & autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® HPX4R PC Copolymer (Europe-Africa-Middle East)
Medium flow specialty polycarbonate with outstanding processability, ductility and autoclavability. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatib..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® OQ4320 PC (Europe-Africa-Middle East)
LEXAN OQ4320 is a medium viscosity grade with a UV cut-off up to 400 nm and a greater optical purity than standard grades. Fields of application for this material are optical lenses, f.i. in sunglas..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® 925 PC (Europe-Africa-Middle East)
Lexan* 925A Polycarbonate (PC) resin is a non-filled, injection moldable grade of non-chlorinated, non-brominated flame retardant systems that has an UL-94 V0 rating. Lexan 925A is available in tran..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® 925AU PC (Europe-Africa-Middle East)
Lexan* 925AU Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is UV stabilized, providing addit..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 6.40 mm |
255
°F @Thickness 0.252 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® BFL4000U PC
Lexan* BFL4000U Polycarbonate resin is an injection moldable grade. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0 rating and good impact/flow balance. Designed fo..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL1414 PC Copolymer (Europe-Africa-Middle East)
Lexan* EXL1414 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade. This resin offers extreme low temperature (-40 C) ductility in combination with excel..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® EXL9330 PC Copolymer (Asia Pacific)
Opaque PC-Siloxane copolymer with excellent processability. Non-chlorinated, non-brominated flame retardant product in most colors. UV-stabilized. UL rated f1/V-0/5VA.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FXD1413T PC Copolymer (Europe-Africa-Middle East)
Clear PC-siloxane copolymer with excellent processability, in special light diffusion colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may af..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics Lexan® FXE1413T PC Copolymer (Asia Pacific)
Clear PC-siloxane copolymer with excellent processability, for Visual fX capability in "Energy" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color packa..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics Lexan® SLX2271T PC Copolymer
Low viscosity PC copolymer blend with enhanced UV stabilization and added release agent. V2 rated. Available in transparent and tinted colors
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics PC1800 PC (Asia Pacific)
PC1800 resin is a medium-high flow (MFR = 18 at 300ºC/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 3.20 mm |
255
°F @Thickness 0.126 in |
ASTM D 648 |
|
SABIC Innovative Plastics PC1803R PC
PC1803R resin is a medium-high flow (MFR = 18 at 300ºC/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
124
°C @Thickness 6.40 mm |
255
°F @Thickness 0.252 in |
ASTM D648 |
|
Samsung Cheil Industries Infino® GW-1030S PC, Unreinforced Recycled
Eco-friendly Post-Consumer recycled content.Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ISO 75-1,-2 |
|
Covestro Makrolon® 1954 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Low viscosity• UV st..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ISO 75-1,-2 |
|
Covestro Makrolon® 2407 MAS145 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ISO 75-1/-2 |
|
Covestro Makrolon® 2867 Polycarbonate, Flame Retardant Grade
ISO 7391-PC,MFLR,(,,)-09-9MVR (300 °C/1.2 kg) 9.5 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-2/1.5 mm and 3.0 mmMedium viscosityUV stabilizedEasy releaseInjection molding - Melt tem..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | ASTM D648 |
|
Entec Hypro™ PPH-GF10 Natural Homopolymer Polypropylene, 10% Glass Reinforced