Polymer Property : Linear Mold Shrinkage, Transverse = 0.0080 in/in Product List
Physical PropertiesTips: 30 items are displayed at most.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0060
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® CFR7431 PC COPOLYMER (Asia Pacific)
Lexan* CFR7431 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm an..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer
Lexan* EXL1112 polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent ..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer
Lexan* EXL1132 polycarbonate (PC) siloxane copolymer resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high fl..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer (Asia Pacific)
Lexan* EXL1132 polycarbonate (PC) siloxane copolymer resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high fl..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1162T PC Copolymer (Asia Pacific)
Lexan* EXL1162T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding (IM) grade with extra release properties. This resin offers good low temperature (-20 C) ductility in c..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1434 PC Copolymer (Europe-Africa-Middle East)
Lexan* EXL1434 polycarbonate (PC) siloxane copolymer resin is a medium flow opaque injection molding (IM) grade and is UV stabilized. This resin offers extreme low temperature (-40 C), exhibits exce..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer
Lexan* EXL1464T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flo..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Europe-Africa-Middle East)
Lexan* EXL1464T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flo..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® FXG1413T PC Copolymer (Asia Pacific)
PC-siloxane copolymer in special ""Diamond Sparkle"" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® HPX8R PC Copolymer
Very high flow specialty polycarbonate with outstanding processability and ductility. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 o..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0060
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® LUX7430C PC COPOLYMER
Lexan* LUX7430C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm a..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0060
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® LUX7432C PC COPOLYMER
Lexan* LUX7432C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm a..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL1414T PC Copolymer (Asia Pacific)
Lexan* EXL1414T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flo..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® EXL9132 PC Copolymer (Europe-Africa-Middle East)
Opaque PC-Siloxane copolymer with excellent processability. Improved flow, low temperature ductility, UV stabilized. Non-chlorinated, non-brominated flame retardant product. UL rated V0/5VA.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0060
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® LUX7632C PC COPOLYMER (Europe-Africa-Middle East)
Lexan* LUX7632C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Time 86400 sec |
0.0060
-
0.0080
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL12 PC
LNP* Lubricomp* DFL12 is a compound based on Polycarbonate resin containing 10% Glass Fiber and 5% PTFE. Added features include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Time 86400 sec |
0.0060
-
0.0080
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL42 PC
LNP* Lubricomp* DFL-4042 a compound based on Polycarbonate resin containing 10% Glass Fiber, 20% PTFE. Added features include: Internally Lubricated.
|
|||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
|
Idemitsu Kosan Xarec® N WA 7020 SPS, 20% Glass Filled
Crystalline Polymer Blend, Glass Filled, Impact Modified. Used in Automotive Electronics applications.
|
|||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
|
LATI Latilub 80-10T Y/15 PPS, 15% Aramid Fiber Reinforced, PTFE Filled
Self-lubricating product based on Polyphenylene Sulfide (PPS). PTFE. Aramid fibers. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | |
|
LATI Latilub 80-40GRT PPS, Graphite/PTFE Filled
Self-lubricating product based on Polyphenylene Sulfide (PPS). Graphite / PTFE. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Ind..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0060
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Ultem HFATX200 PEI+PCE (Asia Pacific)
High flow Polyetherimide blend with internal mold release. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0040
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0040
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Valox® IQ507 PBT+PC
Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characte..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Time 86400 sec |
0.0060
-
0.0080
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF002 PC
LNP THERMOCOMP* DF002 is a compound based on Polycarbonate resin containing 10% Glass Fiber.
|
|||
| Linear Mold Shrinkage, Transverse |
0.0050
-
0.0080
cm/cm @Time 86400 sec |
0.0050
-
0.0080
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF006HL PC
LNP THERMOCOMP* DF006HL is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material include: Low Extractible, Healthcare.
|
|||
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on Tensile Bar; SABIC Method |
|
SABIC Innovative Plastics Valox® IQNH4565 PBT (Asia Pacific)
Valox* iQNH4565 resin is a non-brominated/non-chlorinated flame retardant product based on an environmentally sustainable Valox iQ* PBT resin. Post-consumer recycle (PCR) usage is 29% based on EPEAT..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Time 86400 sec |
0.0060
-
0.0080
in/in @Time 24.0 hour |
ASTM D955 |
|
SABIC Innovative Plastics LNP THERMOCOMP PX87791 PA 6
LNP* THERMOCOMP* PX87791 is a compound based on Nylon 6 resin containing Proprietary Filler(s).
|
|||
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | |
|
E-Polymers TEKAMID® JN930 PPE+PA66 30% Glass Fiber Reinforced PA/PPE Alloy
Polyamide (Nylon) Resin. TEKAMID is widely being used in manufacturing of automotive and industrial parts with its outstanding mechanical, thermal and chemical properties.JN-series: PA66/PPE, PA6/P..
|
|||
| Linear Mold Shrinkage, Transverse |
0.0060
-
0.0080
cm/cm @Thickness 3.20 mm |
0.0060
-
0.0080
in/in @Thickness 0.126 in |
SABIC Method |
|
SABIC Innovative Plastics Lexan® LUX7632C PC COPOLYMER (Asia Pacific)
Lexan* LUX7632C Polycarbonate (PC) resin is a non-filled, extrudable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.0 mm / 5VA rating at 3.0mm and is U..
|
|||
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ISO 294-4 |
|
Polyplastic Armlen® PP GF 30-1EX Polypropylene Copolymer, 30% Glass Fiber
Information provided by PolyPlastic Group.
|
|||