Polykemi AB SCANCOMP PP BN140 T5 Polypropylene

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer Polykemi AB
Trade Name SCANCOMP PP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANCOMP PP BN140 T5 Polypropylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
ISO 1183
Linear Mold Shrinkage 0.015 cm/cm
0.015 in/in
Across Flow; ISO 2577
0.015 cm/cm
0.015 in/in
With Flow; ISO 2577
Melt Index of Compound 14 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 14 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 35.0 MPa
<= 5080 psi
ISO/R527
Flexural Strength <= 60.0 MPa
<= 8700 psi
ISO 178
Flexural Modulus 2.50 GPa

@Temperature 23.0 °C
 363 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched 4.80 J/cm²

@Temperature 23.0 °C
 22.8 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 0.150 J/cm²

@Temperature -20.0 °C
 0.714 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.450 J/cm²

@Temperature 23.0 °C
 2.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 66.0 °C
151 °F
120°C/h; ISO 75/1
Vicat Softening Point 94.0 °C

@Load 5.001 kg
 201 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in