Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
Manufacturer | BASF |
Trade Name | Polystyrol® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | BASF Polystyrol® 2710 Impact Grade Polystyrene (Europe).pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.05 g/cc | 0.0379 lb/in³ | |
Water Absorption | 0.10 % | 0.10 % | |
Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
Linear Mold Shrinkage, Flow | 0.0055 cm/cm | 0.0055 in/in | |
Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Yield | 21.0 MPa | 3050 psi | |
Elongation at Break | 35 % | 35 % | |
Elongation at Yield | 1.7 % | 1.7 % | |
Tensile Modulus | 1.50 GPa | 218 ksi | |
Charpy Impact Unnotched | NB | NB | |
12.0 J/cm² @Temperature -30.0 °C |
57.1 ft-lb/in² @Temperature -22.0 °F |
||
Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | |
Vicat Softening Point | 89.0 °C | 192 °F | |
Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
|
Oxygen Index | 18 % | 18 % |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
Dissipation Factor | 0.00010 @Frequency 1e+6 Hz |
0.00010 @Frequency 1e+6 Hz |
|
Comparative Tracking Index | 500 V | 500 V |