RheTech Products M25P251-01 25% Mica Reinforced Polypropylene Copolymer, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Mica Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products M25P251-01 25% Mica Reinforced Polypropylene Copolymer, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Fan shroudsGlove box binFiller panelsClose-out panelsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 25 % | 25 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 20.0 MPa | 2900 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 2.14 GPa | 310 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature 23.0 °C |
1.30 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 2.26 J | 1.67 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 227 °C | 390 - 440 °F | |
| Middle Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Front Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Nozzle Temperature | 216 - 227 °C | 420 - 440 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 10.3 MPa | 400 - 1500 psi | |
| Hold Pressure | 2.07 - 8.27 MPa | 300 - 1200 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- PlastiComp Complet® LGF50-PPA Polyphthalamide, 50% Long Glass Fiber Reinforced
- Kraton® FG1901 + PBT blend (30/70), Oven Aged
- Heatbath/Park Alu-Braze 930 Aluminum Brazing Salt
- Multibase Multi-Flex® A 4541 Clear TPE Thermoplastic Elastomer
- Teknor Apex Chemlon® 345G Nylon 610, Glass Fiber Reinforced
- Teknor Apex Monprene® MP-1357A Thermoplastic Elastomer
- Cotronics Duralco™ 132 500°F (260°C) Aluminum Filled Epoxy
- ConocoPhillips Hydroclear® 60 Fluid
- 3M Scotchcast™ 265 Electrical Epoxy Powder Resin
- SABIC Innovative Plastics LNP THERMOCOMP JF002 PES
Copyright © lookpolymers.com All Rights Reserved