Hexcel® HexPly® F650 Bismaleimide Resin with Fiberglass 7781 fabric reinforcement

Category Polymer , Thermoset , Polyimide, TS
Manufacturer Hexcel
Trade Name HexPly®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexPly® F650 Bismaleimide Resin with Fiberglass 7781 fabric reinforcement.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Laminate Physicals: 53% Fiber volume, 29% Resin content, 0.5% VoidsInformation provided by HexCel
Mechanical Properties Metric English Comments
Tensile Strength, Yield 342 MPa

@Temperature 177 °C
 49600 psi

@Temperature 351 °F
355.8 MPa

@Temperature 232 °C
 51600 psi

@Temperature 450 °F
418.5 MPa

@Temperature 23.0 °C
 60700 psi

@Temperature 73.4 °F
Tensile Modulus 23.1 GPa

@Temperature 232 °C
 3350 ksi

@Temperature 450 °F
25.5 GPa

@Temperature 177 °C
 3700 ksi

@Temperature 351 °F
29.5 GPa

@Temperature 23.0 °C
 4280 ksi

@Temperature 73.4 °F
Flexural Yield Strength 219.9 MPa

@Temperature 232 °C
 31890 psi

@Temperature 450 °F
 Wet condition - 96 hours in boiling H2O
319.2 MPa

@Temperature 177 °C
 46300 psi

@Temperature 351 °F
 Wet condition - 96 hours in boiling H2O
541.2 MPa

@Temperature 232 °C
 78490 psi

@Temperature 450 °F
541.9 MPa

@Temperature 177 °C
 78600 psi

@Temperature 351 °F
637.8 MPa

@Temperature 23.0 °C
 92510 psi

@Temperature 73.4 °F
Flexural Modulus 22.5 GPa

@Temperature 232 °C
 3260 ksi

@Temperature 450 °F
 Wet condition - 96 hours in boiling H2O
24.8 GPa

@Temperature 177 °C
 3600 ksi

@Temperature 351 °F
 Wet condition - 96 hours in boiling H2O
27.8 GPa

@Temperature 232 °C
 4030 ksi

@Temperature 450 °F
28.2 GPa

@Temperature 177 °C
 4090 ksi

@Temperature 351 °F
31.1 GPa

@Temperature 23.0 °C
 4510 ksi

@Temperature 73.4 °F
Compressive Yield Strength 175.1 MPa

@Temperature 232 °C
 25400 psi

@Temperature 450 °F
 Wet condition - 96 hours in boiling H2O
224.1 MPa

@Temperature 177 °C
 32500 psi

@Temperature 351 °F
 Wet condition - 96 hours in boiling H2O
392.3 MPa

@Temperature 177 °C
 56900 psi

@Temperature 351 °F
392.3 MPa

@Temperature 232 °C
 56900 psi

@Temperature 450 °F
480.6 MPa

@Temperature 23.0 °C
 69710 psi

@Temperature 73.4 °F
Compressive Modulus 23.1 GPa

@Temperature 232 °C
 3350 ksi

@Temperature 450 °F
 Wet condition - 96 hours in boiling H2O
24.9 GPa

@Temperature 177 °C
 3610 ksi

@Temperature 351 °F
 Wet condition - 96 hours in boiling H2O
28.0 GPa

@Temperature 177 °C
 4060 ksi

@Temperature 351 °F
28.1 GPa

@Temperature 232 °C
 4080 ksi

@Temperature 450 °F
31.4 GPa

@Temperature 23.0 °C
 4550 ksi

@Temperature 73.4 °F
Shear Strength 14.2 MPa

@Temperature 232 °C
 2060 psi

@Temperature 450 °F
 Short Beam Shear, Wet condition - 96 hours in boiling H2O
15.9 MPa

@Temperature 177 °C
 2310 psi

@Temperature 351 °F
 Short Beam Shear, Wet condition - 96 hours in boiling H2O
39.4 MPa

@Temperature 232 °C
 5710 psi

@Temperature 450 °F
 Short Beam Shear
53.1 MPa

@Temperature 23.0 °C
 7700 psi

@Temperature 73.4 °F
53.4 MPa

@Temperature 177 °C
 7750 psi

@Temperature 351 °F
 Short Beam Shear