SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp MX96070 PP (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STARFLAM* MX96070 is a compound based on Polypropylene resin containing Flame Retardant. Added features include: Flame Retardant.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm | 0.021 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.8 % | 4.8 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 45.0 MPa | 6530 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 98.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
54.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 125 µm/m-°C @Temperature 23.0 - 60.0 °C |
69.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8960 (498A) (UF) Synthetic Oil
- Qualchem Danamid AFGFS2HUV14 Polyamide 66, 14% Glass Fiber
- Ravago Manufacturing Americas Hylon® N1013THL Nylon 6/6 (Cond)
- Plenco Valite 4100 Novolac Phenolic, Granular, Compression Molded (discontinued **)
- Shakespeare Isocorâ„¢ CN30XT Nylon 610
- Total PPC 11812 S01 Polypropylene, Heterophasic Copolymer, Injection Molding
- Eastman Eastapak 9921 PET
- BASF Lupragen® N 100 DMCHA Dimethylcyclohexylamine
- Ashley Polymers Ashlene® 528L-13G Nylon 66, 13% Glass Reinforced
- Arlon 44571B008 0.0085" (0.216 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved