SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GFN1630V PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Noryl* GFN1630V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 30 % Glass Reinforced, injection moldable grade with improved hydrolytic stability; this grade has been developed for fluid engineering applications. Noryl* GFN1630V has been certified for potable water applications up to 85C in Europe and North America in limited colours.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10 g/10 min @Load 5.00 kg, Temperature 300 °C |
10 g/10 min @Load 11.0 lb, Temperature 572 °F |
ASTM D1238 |
| Melt Index of Compound | 17 g/10 min @Load 10.0 kg, Temperature 300 °C |
17 g/10 min @Load 22.0 lb, Temperature 572 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 130 MPa | 18900 psi | ISO 2039-1 |
| Tensile Strength at Break | 119 MPa | 17300 psi | Type I, 5 mm/min; ASTM D638 |
| 120 MPa | 17400 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 119 MPa | 17300 psi | Type I, 5 mm/min; ASTM D638 |
| 120 MPa | 17400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1 mm/min; ISO 527 |
| 9.10 GPa | 1320 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 175 MPa | 25400 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | 2 mm/min; ISO 178 |
| 7.30 GPa | 1060 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| 0.790 J/cm @Temperature -30.0 °C |
1.48 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D4812 |
| 5.30 J/cm @Temperature -30.0 °C |
9.93 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 70 | 70 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 148 °C @Thickness 3.20 mm |
298 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 149 °C | 300 °F | Rate B/50; ISO 306 |
| 152 °C | 306 °F | Rate B/50; ASTM D1525 | |
| 155 °C | 311 °F | Rate A/50; ISO 306 | |
| 158 °C | 316 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 50.0 - 60.0 Hz |
2.9 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.00060 @Frequency 50.0 - 60.0 Hz |
0.00060 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0010 @Frequency 1.00e+6 Hz |
0.0010 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 110 MEDICAL DEVICES APPROVED (500 Viscosity) Rapid Bonding Adhesive
- Kinlead PG11 Bag Grade BOPP Plain Film (thickness: 40 µm)
- Ineos T50-500 HDPE
- Multibase Dow Corning® MB50-001 Siloxane Additive
- HP Alloys Alloy 718, 20% Cold Worked
- Hexcel® HexWeb® CR III 3/8-5056-.002 Corrosion Resistant Specification Grade Aluminum Honeycomb
- Elmer's Products Aron Alpha® 201 Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- Fainplast Compounds GS 90 Flexible PVC, Injection Molding for Footwear
- Dow Corning Z-6040® SILANE
Copyright © lookpolymers.com All Rights Reserved