PTS Tristar® PC-10R-CL(V6) 6 MFI UV Stabilized Clear Polycarbonate with Release

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Optical Grade
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name Tristar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS Tristar® PC-10R-CL(V6) 6 MFI UV Stabilized Clear Polycarbonate with Release.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ASTM D792
Water Absorption 0.15 %
0.15 %
24 hours at 73°F; ASTM D570
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 62.1 MPa

@Thickness 3.17 mm
 9010 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 150 %

@Thickness 3.17 mm
 150 %

@Thickness 0.125 in
 ASTM D638
Flexural Yield Strength 96.5 MPa

@Thickness 3.17 mm
 14000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.41 GPa

@Thickness 3.17 mm
 350 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 9.08 J/cm

@Thickness 3.17 mm
 17.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.2 µm/m-°C

@Temperature -40.0 - 95.0 °C
 39.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E831-06
CTE, linear, Transverse to Flow 68.4 µm/m-°C

@Temperature -40.0 - 95.0 °C
 38.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E831-06
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
ASTM D648
137 °C
279 °F
ISO 75
UL RTI, Electrical 125 °C
257 °F
UL RTI, Mechanical with Impact 115 °C
239 °F
UL RTI, Mechanical without Impact 125 °C
257 °F
Flammability, UL94 V-2

@Thickness 1.50 mm
 V-2

@Thickness 0.0591 in
Glow Wire Test 775 °C
1430 °F
GWIT
960 °C
1760 °F
GWFI
Optical Properties Metric English Comments
Refractive Index 1.586
1.586
nD
Haze 1.0 %
1.0 %
Transmission, Visible 89 %
89 %
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
PLC 6
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC 2
Hot Wire Ignition, HWI 15 - 30 sec

@Thickness 1.50 mm
 15 - 30 sec

@Thickness 0.0591 in
 PLC 3
30 - 60 sec

@Thickness 3.00 mm
 30 - 60 sec

@Thickness 0.118 in
 PLC 2
High Amp Arc Ignition, HAI 60 - 120 arcs

@Thickness 3.00 mm
 60 - 120 arcs

@Thickness 0.118 in
 PLC 1
>= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
 PLC 0
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC 3
Processing Properties Metric English Comments
Rear Barrel Temperature 288 - 304 °C
550 - 580 °F
Middle Barrel Temperature 299 - 321 °C
570 - 610 °F
Front Barrel Temperature 316 - 338 °C
600 - 640 °F
Nozzle Temperature 304 - 332 °C
580 - 630 °F
Melt Temperature 316 - 343 °C
600 - 650 °F
Mold Temperature 82.2 - 116 °C
180 - 240 °F
Drying Temperature 121 °C
250 °F
Dry Time 3 - 4 hour
3 - 4 hour
48 hours max.
Injection Pressure 110 - 152 MPa
16000 - 22000 psi
Back Pressure 0.345 - 1.38 MPa
50.0 - 200 psi
Clamp Pressure 27.6 - 68.9 MPa
4000 - 10000 psi
Shot Size 40 - 60 %
40 - 60 %
Screw Speed 40 - 70 rpm
40 - 70 rpm
Descriptive Properties Value Comments
Injection Speed- Edge Gate Slow to Medium
Injection Speed- Tab Gate Medium to Fast
Injection Speed- Tunnel Gate Fast