- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 137 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 137 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | ASTM D648 |
|
Proto3000 Duraform® AF Selective Laser Sintering (SLS®) Prototyping Polymer
Description: Polyamide (nylon) material with metallic appearance for real-world physical testing and functional use.Features:Metallic appearance with nice surface finishGood powder recycle character..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 3413HF PC (Asia Pacific)
30% glass reinforced, high flow PC.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® 500RS PC (Europe-Africa-Middle East)
LEXAN 500RS is a medium viscosity, glass reinforced, flame retardant grade.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 505RU PC
Lexan* 505RU is a glass reinforced,flame retardant(FR)grade with non brominated and non chlorinated FR systems and UV stablization packages. This product is intended for applications to meet WEEE/Ro..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® 505RU PC (Europe-Africa-Middle East)
Lexan* 505RU is a 10% glass reinforced,flame retardant(FR)grade with non brominated and non chlorinated FR systems and UV stablization packages. This product is intended for applications to meet WEE..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics Lexan® EXL4019 PC (Asia Pacific)
Lexan* EXL4019 is an opaque 9% Glass Fiber (GF) reinforced polycarbonate (PC) siloxane copolymer resin for injection molding (IM) applications requiring improved stiffness. This resin also offers im..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | ISO 75 |
|
PTS Tristar® PC-10R-(V15) 15 MFI UV Stabilized Polycarbonate With Release
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | ISO 75 |
|
PTS Tristar® PC-10R-(V20) 20 MFI UV Stabilized Polycarbonate with Release
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | ISO 75 |
|
PTS Tristar® PC-10R-CL(V6) 6 MFI UV Stabilized Clear Polycarbonate with Release
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP DFL349EF PC
LNP LUBRICOMP* DFL349EF is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | ISO 75 |
|
PTS Tristar® PC-10R-CL(6) 6 MFI Clear Polycarbonate with Release
Information provided by Polymer Technology and Services, LLC (PTS).
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRILOY DF204 PC
LNP* LUBRILOY* DF204 is a compound based on Polycarbonate resin containing 20% Glass Fiber, Proprietary Lubricant. Added feature of th is grade is: Wear Resistant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Unannealed; ISO 75-2/A |
|
Solvay Specialty Polymers Kalix® 3950 Polyamide, High Performance (HPPA), 50% Glass Fiber
Kalix® 3950 is a 16% bio-sourced, amorphous polyphthalamide (PPA)-based compound with 50% by weight glass fiber reinforcement. This material is uniquely formulated to prevent warpage and flash in..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DEL139P PC
LNP* STAT-KON* DEL139P is a compound based on Polycarbonate containing 15% Carbon Fiber, 5% PTFE. Added features of this grade include: Electrically Conductive, Exceptional Processing, Flame Retar..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Stat-kon ZE004 MODIFIED POYPHENYLENE (Asia Pacific)
LNP* Stat-kon* ZE004 is a compound based on MODIFIED POYPHENYLENE resin containing Carbon Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP DF002ERH PC
LNP THERMOCOMP* DF002ERH is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Healthcare, Mold Release.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP DF0046P PC (Asia Pacific)
LNP* Thermocomp* DF0046P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing, Flame Retardant, Non-Br..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP DX06411 PC (Asia Pacific)
LNP* Thermocomp* DX06411 is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Samsung Cheil Industries Infino® HN-3102G PC, Glass Filled FR
Information provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 6.40 mm
|
279
°F <br>@Thickness 0.252 in
|
ASTM D648 |
|
Samsung Cheil Industries Infino® LB-3150GW PC, 15% Glass Filled High Impact
High-impact resistant PC/GF that can be used for middle mold frame of LCD TVInformation provided by Samsung Cheil Industries.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | annealed; ISO 75-A |
|
Styron CALIBREâ„¢ 280-25 Polycarbonate
CALIBREâ„¢ PC Utility Grade 280-15 is a high flow opaque polycarbonate with an internal mold release system. Applications: Internal parts Electrical Electronics Lightning Information provided b..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics NORYL NH7112 PPE+HIPS (Europe-Africa-Middle East)
Noryl* NH7112 resin is a 10% glass reinforced, modified PPE-PS blend. The material offers an exceptional balance of strength and dimensional stability while using non-halogenated flame retardants to..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP STAT-KON DEP23FXC PC (Asia Pacific)
LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP STAT-KON DX09301C PC (Asia Pacific)
Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconductor and Hard Disk Drive (HDD) application.Added features of this material include: Clean Compounding Sys..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
137
°C <br>@Thickness 3.20 mm
|
279
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP DC0049XF PC (Asia Pacific)
LNP* Thermocomp* DC0049XF is a compound based on Polycarbonate resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, , Flame Retardant.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP DF002ER PC
LNP THERMOCOMP* DF002ER is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding. Mold Release
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Thermocomp XF006S
LNP* Thermocomp* XF006S is a compound based on Amorphous Nylon containing Glass Fiber. Characteristics of this grade are: Heat Stabilized.This data was supplied by SABIC-IP for the Americas region..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
|
SABIC Innovative Plastics Lexan® ML3260 PC (Europe-Africa-Middle East)
LEXAN ML3260 is a medium viscosity, 15% glass reinforced, flame retardant grade especially designed for applications like computer cartridges.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | 0.25 inch; ASTM D648 |
|
PlastxWorld CEVIAN® S5230 30% GF PC/ABS alloy
Glass fiber reinforced and flame retarded PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | 80*10*4 s=60mm; ISO 75-1 a |
|
Sax Polymers SAXALEN PPH304G25 Polypropylene Homopolymer, 25% Glass Filled
SAXALEN PPH304G25 is a 25% glass filled Polypropylene - Homopolymer intended for injection molding. This compound is characterized by high stiffness good impact resistance und reduced creep under lo..
|
|||