Chi Mei Kibisan® PN-127 SAN
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | Chi Mei Corporation (ChiMei) |
| Trade Name | Kibisan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chi Mei Kibisan® PN-127 SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Heat Resistant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| 6.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
6.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 | |
| 17 g/10 min @Load 10.0 kg, Temperature 220 °C |
17 g/10 min @Load 22.0 lb, Temperature 428 °F |
Melt Volume Rate (ml/10 min); ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 164 MPa | 23800 psi | H358/30; ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 77.0 MPa | 11200 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 7.0 % | 7.0 % | 50 mm/min; ISO 527 |
| Flexural Strength | 105 MPa | 15200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.176 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.330 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 |
| 0.198 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.370 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1C |
| Charpy Impact Unnotched | 2.10 J/cm² | 9.99 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Impact | 3.00 | 3.00 | Impact Flexural Test Notched (KJ/m²) |
| 24.0 | 24.0 | Impact Flexural Test Unnotched (KJ/m²) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C | 189 °F | unannealed; ISO 75 |
| 98.0 °C | 208 °F | annealed; ISO 75 | |
| Vicat Softening Point | 104 °C @Load 5.00 kg |
219 °F @Load 11.0 lb |
50°C/hr; ISO 306 |
| 104 °C @Load 5.00 kg |
219 °F @Load 11.0 lb |
120°C/hr; ISO 306 | |
| 107 °C @Load 1.00 kg |
225 °F @Load 2.20 lb |
50°C/hr; ISO 306 | |
| 110 °C @Load 1.00 kg |
230 °F @Load 2.20 lb |
120°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
UL 94 |
Users viewing this material also viewed the following:
- PPT BP860 NiZn Ferrite Powder
- SABIC Innovative Plastics Lexan® HP6 PC
- Lucent Polymers CPP-340 Polypropylene, 40% Calcium Carbonate Filled, Impact Modified
- Schott BG38 Band Pass Filter
- SABIC Innovative Plastics Ultem DT1800E PEI Blend (Asia Pacific)
- Special Metals INCONEL® 686 Nickel Superalloy (UNS N06686) Plate 0.250 in (6.4 mm)
- Universal Wire Works BCo-1 (AMS 4783) Nickel Base Brazing Filler Metal
- Goodfellow Cobalt 90/Aluminum 10 Alloy
- Eastman Eastar BR203 Copolyester
- Bostik 2106 Low viscosity, quick grab EVA Glue Stick
Copyright © lookpolymers.com All Rights Reserved