LG Chemical LI911 ASA

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical LI911 ASA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Good Weatherability, High FlowApplication: Air-conditioner grill, Sawing Machine Cover, Electric/Electronic ApplicationsCAS: 26299-47-8Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 20 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 20 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 107
107
ASTM D785
Tensile Strength, Yield 49.0 MPa

@Thickness 3.20 mm
 7110 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 20 %

@Thickness 3.20 mm
 20 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Yield >= 6.0 %

@Thickness 3.20 mm
 >= 6.0 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Tensile Modulus 2.17 GPa

@Thickness 3.20 mm
 314 ksi

@Thickness 0.126 in
 1mm/min; ASTM D638
Flexural Yield Strength 78.5 MPa

@Thickness 3.20 mm
 11400 psi

@Thickness 0.126 in
 15mm/min; ASTM D790
Flexural Modulus 2.30 GPa

@Thickness 3.20 mm
 334 ksi

@Thickness 0.126 in
 15mm/min; ASTM D790
Izod Impact, Notched 0.294 J/cm

@Thickness 3.20 mm,
Temperature -30.0 °C
 0.551 ft-lb/in

@Thickness 0.126 in,
Temperature -22.0 °F
 ASTM D256
0.294 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 0.551 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
1.18 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 2.20 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
1.37 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 2.57 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C

@Thickness 6.40 mm
 205 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 6.40 mm
 189 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 96.0 °C

@Load 5.00 kg
 205 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
50.0 °C

@Thickness >=6.00 mm
 122 °F

@Thickness >=0.236 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
50.0 °C

@Thickness >=6.00 mm
 122 °F

@Thickness >=0.236 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
50.0 °C

@Thickness >=6.00 mm
 122 °F

@Thickness >=0.236 in
Flammability, UL94 HB

@Thickness >=1.60 mm
 HB

@Thickness >=0.0630 in
HB

@Thickness >=3.20 mm
 HB

@Thickness >=0.126 in
HB

@Thickness >=6.00 mm
 HB

@Thickness >=0.236 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Dielectric Strength 27.0 kV/mm
686 kV/in
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
 7.0 - 15 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
 15 - 30 sec

@Thickness >=0.118 in
15 - 30 sec

@Thickness >=6.00 mm
 15 - 30 sec

@Thickness >=0.236 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
>= 120 arcs

@Thickness 6.00 mm
 >= 120 arcs

@Thickness 0.236 in
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Front Barrel Temperature 210 - 220 °C
410 - 428 °F
Injection Molding
Nozzle Temperature 210 - 220 °C
410 - 428 °F
Injection Molding
Melt Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Injection Molding
Drying Temperature 80.0 - 90.0 °C
176 - 194 °F
Injection Molding
Dry Time 2.00 - 3.00 hour
2.00 - 3.00 hour
Injection Molding
Back Pressure 0.490 - 0.981 MPa
71.1 - 142 psi
Injection Molding
Screw Speed 50 - 100 rpm
50 - 100 rpm
Injection Molding