LG Chemical HF380NS ABS, High Flow, General Anti-Static

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer LG Chemical
Trade Name
Port Ningbo port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF LG Chemical HF380NS ABS, High Flow, General Anti-Static.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Feature: Injection Molding, High Flow, General Anti-StaticApplication: Electric & Electronic Products, Miscellaneous goods)CAS No. 9003-56-9Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.04 g/cc
1.04 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
<br>@Thickness 3.20 mm
 0.0040 - 0.0070 in/in
<br>@Thickness 0.126 in
 ASTM D955
Melt Flow 43 g/10 min
<br>@Load 10.0 kg,<br> Temperature 220 °C
 43 g/10 min
<br>@Load 22.0 lb,<br> Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 106
106
ASTM D785
Tensile Strength, Yield 42.2 MPa
<br>@Thickness 3.20 mm
 6120 psi
<br>@Thickness 0.126 in
 50 mm/min; ASTM D638
Elongation at Break 40 %
<br>@Thickness 3.20 mm
 40 %
<br>@Thickness 0.126 in
 50 mm/min; ASTM D638
Flexural Yield Strength 68.6 MPa
<br>@Thickness 3.20 mm
 9960 psi
<br>@Thickness 0.126 in
 15 mm/min; ASTM D790
Flexural Modulus 2.45 GPa
<br>@Thickness 3.20 mm
 356 ksi
<br>@Thickness 0.126 in
 15 mm/min; ASTM D790
Izod Impact, Notched 2.35 J/cm
<br>@Thickness 6.40 mm,<br> Temperature 23.0 °C
 4.41 ft-lb/in
<br>@Thickness 0.252 in,<br> Temperature 73.4 °F
 ASTM D256
2.35 J/cm
<br>@Thickness 3.20 mm,<br> Temperature 23.0 °C
 4.41 ft-lb/in
<br>@Thickness 0.126 in,<br> Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
<br>@Thickness 6.40 mm
 183 °F
<br>@Thickness 0.252 in
 Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
 UL 746B
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical with Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
 UL 746B
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
UL RTI, Mechanical without Impact 60.0 °C
<br>@Thickness >=1.50 mm
 140 °F
<br>@Thickness >=0.0591 in
 UL 746B
60.0 °C
<br>@Thickness >=3.00 mm
 140 °F
<br>@Thickness >=0.118 in
Flammability, UL94 HB
<br>@Thickness >=1.50 mm
 HB
<br>@Thickness >=0.0591 in
HB
<br>@Thickness >=3.00 mm
 HB
<br>@Thickness >=0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
Dielectric Strength 34.0 kV/mm
864 kV/in
Arc Resistance 60 - 120 sec
60 - 120 sec
ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
Solution A; IEC 60112
Hot Wire Ignition, HWI 15 - 30 sec
<br>@Thickness >=1.50 mm
 15 - 30 sec
<br>@Thickness >=0.0591 in
15 - 30 sec
<br>@Thickness >=3.00 mm
 15 - 30 sec
<br>@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs
<br>@Thickness 1.50 mm
 >= 120 arcs
<br>@Thickness 0.0591 in
>= 120 arcs
<br>@Thickness 3.00 mm
 >= 120 arcs
<br>@Thickness 0.118 in
High Voltage Arc-Tracking Rate, HVTR 10.0 - 25.4 mm/min
0.394 - 1.00 in/min
Processing Properties Metric English Comments
Rear Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Middle Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Front Barrel Temperature 200 - 220 °C
392 - 428 °F
Injection Molding
Nozzle Temperature 200 - 230 °C
392 - 446 °F
Injection Molding
Melt Temperature 210 - 240 °C
410 - 464 °F
Injection Molding
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding