A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Bead Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 6 GF33RN 33% Glass Bead Reinforced, Industrial Grade Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.175 mm |
0.010 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 147 MPa | 21300 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 230 MPa | 33400 psi | ASTM D790 |
| Flexural Modulus | 8.4681 GPa | 1228.2 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.7 J/cm | 22.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
Users viewing this material also viewed the following:
- PSM Industries PolyAlloys MIM-WC-9Co Tungsten Carbide
- EVALCA EVAL® G156A Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
- Momentive Performance Materials HCPL Boron Nitride (BN) Powder
- Sylvin Technologies 9980-80 Natural PVC Molding Compound
- Sylvin Technologies 9999-95 Natural PVC Molding Compound
- A. Schulman LP544-01 High-Density Copolymer Polyethylene
- Zeon Chemicals Nipol® 1032-45 Nitrile Elastomer
- Zotefoams Plastazote® LD15IC Low Density Polyethylene Foam, Intermediate Cell
- Cossa Polimeri ESTAPROP H 1660 GFC Polypropylene, 30% Glass Filled
- Axiall 419-90D Coax & Telecom Flexible PVC
Copyright © lookpolymers.com All Rights Reserved