SABIC Innovative Plastics LNP THERMOCOMP RX07034 PA 66 (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP THERMOCOMP RX07034 PA 66 (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Thermocomp* RX07034 is a compound based on PA 66 resin containing Glass Fiber. Added features include; Low Smoke, Easy Molding, Cross Linkable under Beta-or Gamma Radiation; Specially developed for Arc chambers.

Physical Properties	Metric	English	Comments
Density	1.54 g/cc	0.0556 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0030 - 0.0050 cm/cm	0.0030 - 0.0050 in/in	SABIC Method
Melt Index of Compound	70 g/10 min @Load 5.00 kg, Temperature 275 Â°C	70 g/10 min @Load 11.0 lb, Temperature 527 Â°F	MVR [cm^3/10 min]; ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	170 MPa	24700 psi	5 mm/min; ISO 527
Elongation at Break	2.3 %	2.3 %	5 mm/min; ISO 527
Flexural Strength	225 MPa	32600 psi	2 mm/min; ISO 178
Flexural Modulus	9.50 GPa	1380 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	9.00 kJ/mÂ²	4.28 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	60.0 kJ/mÂ²	28.6 ft-lb/inÂ²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	213 Â°C	415 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in	UL 94 by SABIC-IP