Polymer Resources PC/TP-GP1 PC Polyester, High Impact, Good Chemical Resistance (Unverified Data**)

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PC/TP-GP1 PC Polyester, High Impact, Good Chemical Resistance (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0050 - 0.0080 cm/cm	0.0050 - 0.0080 in/in	ASTM D955
Melt Flow	5.0 - 15 g/10 min	5.0 - 15 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	55.2 MPa	8000 psi	ASTM D638
Tensile Strength, Yield	54.5 MPa	7900 psi	ASTM D638
Flexural Strength	82.7 MPa	12000 psi	ASTM D790
Flexural Modulus	2.17 GPa	315 ksi	ASTM D790
Izod Impact, Notched	8.01 J/cm	15.0 ft-lb/in	ASTM D256
Gardner Impact	>= 36.2 J	>= 26.7 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	121 °C	250 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	110 °C	230 °F	ASTM D648
Flammability, UL94	HB	HB	1/16 in
	HB	HB	1/8 in

Processing Properties	Metric	English
Rear Barrel Temperature	249 - 271 °C	480 - 520 °F
Middle Barrel Temperature	254 - 277 °C	490 - 530 °F
Front Barrel Temperature	260 - 282 °C	500 - 540 °F
Melt Temperature	246 - 274 °C	475 - 525 °F
Mold Temperature	65.6 - 87.8 °C	150 - 190 °F
Drying Temperature	104 - 110 °C	220 - 230 °F
Dry Time	4 - 6 hour	4 - 6 hour