Thermoseal KLINGERSIL® C-8200 Chemical Resistant Gasketing
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Chlorosulfonated Polyethylene Rubber |
| Manufacturer | Thermoseal Inc. |
| Trade Name | KLINGERSIL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Thermoseal KLINGERSIL® C-8200 Chemical Resistant Gasketing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Synthetic FiberHypalon® BinderAcid ResistantGood Oil-Fuel ResistanceGood Gas SealabilityNo Color AddedInformation provided by Thermoseal Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in³ | ASTM F1315 |
| Thickness | 1588 microns | 62.52 mil | Thickness tested |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 9.00 kV/mm | 229 kV/in | ASTM D149-95a |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Off White | (Top/Bottom) |
| Compressibility | 9 percent | ASTM F36J |
| Creep Relaxation | 30 percent | 1/32", ASTM F38B |
| Gas Permeability | <0.5 ml/min | DIN 3535/6 |
| Klinger Hot Compression Test | 17 percent | Additional, Thickness Decrease 572°F (300°C), tested at 3,625-psi gasket stress, and to 392°F [200°C] |
| 7 percent | Initial, Thickness Decrease 73°F (23°C), tested at 3,625-psi gasket stress, and to 392°F [200°C] | |
| Recovery | >50 percent | ASTM F36J |
| Sealability | <0.3 ml/hr | 1/32", ASTM F37A |
| Thickness Increase | 0-10% | ASTM Fuel B, 5h/73°F (23°C) |
| 0-5% | ASTM F146 after immersion in ASTM Oil 1, 5h/300°F (149°C) | |
| 0-5% | ASTM Fuel A, 5h/73°F (23°C) | |
| 5-10% | ASTM Oil IRM903, 5h/300°F (149°C) | |
| Weight Increase | <25% | ASTM F146 after immersion in Fuel B 5h/73°F (23°C) |
Users viewing this material also viewed the following:
- Nye Lubricants 734B (RL) Synthetic Oil
- NOVA Chemicals Novapol® LM-0724-A LDPE Injection Molding Resin
- MarkeTech BGO (Bismuth Germanate, Bi4Ge3O12) Scintillator Crystal
- Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate
- Multibase Multi-Flex® TPE A 5401 BLK
- Lehmann & Voss LUVOCOM® 1850-7557 PBT, with aramid reinforcement and PTFE
- Loctite® 713 Accelerator for cyanoacrylates
- Anderman Ceramics EC70P Mullite-Bonded Porous Silicon Carbide (70%)
- Arlon 55100R030 0.030" (0.762 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved