Zhejiang Double Fish YS-G030 30% Long Fiber Glass Reinforced Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Zhejiang Double Fish Plastics Co., Ltd |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Zhejiang Double Fish YS-G030 30% Long Fiber Glass Reinforced Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features high strength, good surface quality, and easy processing. Typical applications include automobile (bumper back beam, arm rest core, instrument panel, mudflap), machinery, electronics, communications (bobbin, relay bed, optical cable closure), military, sports equipment (skis, helmets, foot wear), and medical equipment. Product is customizable.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | Glass Fiber |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 6.25 GPa | 906 ksi | ASTM D790 |
| Izod Impact Resistance | 2.00 J/cm² | 9.52 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 216 - 232 °C | 421 - 450 °F | |
| Middle Barrel Temperature | 210 - 227 °C | 410 - 441 °F | |
| Front Barrel Temperature | 204 - 221 °C | 399 - 430 °F | |
| Melt Temperature | 210 - 249 °C | 410 - 480 °F | |
| Mold Temperature | 38.0 - 77.0 °C | 100 - 171 °F | |
| Injection Velocity | 13.0 - 25.0 mm/sec | 0.512 - 0.984 in/sec | |
| Injection Pressure | 69.0 - 103 MPa | 10000 - 14900 psi | |
| Hold Pressure | 34.0 - 69.0 MPa | 4930 - 10000 psi | |
| Back Pressure | 0.170 - 0.340 MPa | 24.7 - 49.3 psi | |
| Screw Speed | 30 - 70 rpm | 30 - 70 rpm |
Users viewing this material also viewed the following:
- Haynes HR-160® alloy, plate, aged 1000 hours at 871°C (1600°F)
- SABIC Innovative Plastics LNP LUBRICOMP QFL32 PA 6/10
- Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Conditioned)
- Hexcel® Redux® 382HU Film Adhesive
- DSM Akulon® Ultraflow™ K-FHG6 Nylon 6-30% Glass Reinforced (European Grade) (Cond)
- DSM Arnite® T06 200 (extrusion) PBT (European and Asian Grade)
- ExxonMobil Vyram™ 9201-55 Thermoplastic Elastomer (discontinued **)
- Schmolz + Bickenbach Holder Block Plastic Mold Steel
- SABIC Innovative Plastics LNP VERTON RV00CEXS PA 66
Copyright © lookpolymers.com All Rights Reserved