- Toyobo T-661 Nylon 66, Standard Grade (Conditioned)
Toyobo T-661 Nylon 66, Standard Grade (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Toyobo |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo T-661 Nylon 66, Standard Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Non-reinforced, Standard GradeInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | (DAM); ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs at 23°C (DAM); ASTM D570 |
| 2.5 % | 2.5 % | 65% R.H. equilibrium (DAM); ASTM D570 | |
| Linear Mold Shrinkage | 0.0060 - 0.012 cm/cm @Thickness 1.00 mm |
0.0060 - 0.012 in/in @Thickness 0.0394 in |
DAM |
| 0.015 - 0.022 cm/cm @Thickness 3.00 mm |
0.015 - 0.022 in/in @Thickness 0.118 in |
DAM |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | ASTM D638 |
| 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
ASTM D638 | |
| Tensile Strength, Ultimate | 28.0 MPa @Temperature 80.0 °C |
4060 psi @Temperature 176 °F |
ASTM D638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 |
| Flexural Strength | 66.0 MPa | 9570 psi | ASTM D790 |
| 40.0 MPa @Temperature 80.0 °C |
5800 psi @Temperature 176 °F |
ASTM D790 | |
| 120 MPa @Temperature -40.0 °C |
17400 psi @Temperature -40.0 °F |
ASTM D790 | |
| Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
| 0.600 GPa @Temperature 80.0 °C |
87.0 ksi @Temperature 176 °F |
ASTM D790 | |
| 4.00 GPa @Temperature -40.0 °C |
580 ksi @Temperature -40.0 °F |
ASTM D790 | |
| Izod Impact, Notched | 0.400 J/cm @Temperature -40.0 °C |
0.749 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 3.00 J/cm @Temperature 23.0 °C |
5.62 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | ASTM D257 |
| Dielectric Constant | 6.5 @Frequency 1000 Hz |
6.5 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 13.0 kV/mm @Thickness 2.00 mm |
330 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | (DAM) |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | (DAM) |
| Injection Pressure | 30.0 - 40.0 MPa | 4350 - 5800 psi | (DAM) |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® GM 20 R Low Density Polyethylene - Coating Grade
- Ravago Manufacturing Americas Hylon® N1040MHL Nylon 6/6 (DAM)
- Lendell Parapet HH-1000L PMMA, Heat Resistant
- Lanxess Durethan® AKV 30 000000 Nylon 66, Glass Fiber Reinforced
- Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK)
- Styrolution PS 5410 HIPS
- DuPont Vamac® GXF Sample Compound Vulcanizate Slab Cure (5 minutes at 190°C)
- Zylog Neoplast® 180 FT EB Thermoplastic Vulcanizate
- American Elements Boron Nitride Nanoparticles
- BASF Ultradur B 4300 G2 High Speed Unc. 10% Glass Filled PBT
Copyright © lookpolymers.com All Rights Reserved