Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK)

Category Polymer , Thermoplastic , Polyketone
Manufacturer Solvay Specialty Polymers
Trade Name AvaSpire®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-848 Polyaryletherketone (PAEK).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire® AV-848 is a high-temperature, polyaryletherketone (PAEK) that offers several key performance advantages over comparable grades of PEEK above 150°C, including better dimensional stability, lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature.Features: Ductile; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Impact Resistance; High Heat ResistanceUses: Oil/Gas Applications; SealsInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792
Water Absorption 0.50 %

@Time 86400 sec
0.50 %

@Time 24.0 hour
ISO 62
Viscosity 500000 cP
500000 cP
Melt Viscosity; ASTM D3835
Mechanical Properties Metric English Comments
Tensile Strength 94.0 MPa
13600 psi
50 mm/min; ASTM D638
Elongation at Break 35 %
35 %
50 mm/min; ASTM D638
75 %
75 %
5.1 mm/min; ASTM D638
Elongation at Yield 6.7 %
6.7 %
50 mm/min; ASTM D638
Tensile Modulus 3.10 GPa
450 ksi
50 mm/min; ASTM D638
Flexural Strength 134 MPa
19400 psi
ASTM D790
Flexural Modulus 3.30 GPa
479 ksi
ASTM D790
Compressive Strength 118 MPa
17100 psi
ASTM D695
Shear Strength 82.0 MPa
11900 psi
ASTM D732
Izod Impact, Notched 0.750 J/cm
1.41 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D256
Thermal Properties Metric English Comments
Specific Heat Capacity 1.65 J/g-°C

@Temperature 50.0 °C
0.394 BTU/lb-°F

@Temperature 122 °F
ASTM C351
1.66 J/g-°C

@Temperature 200 °C
0.397 BTU/lb-°F

@Temperature 392 °F
ASTM C351
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 340 °C
644 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 252 °C
486 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 158 °C
316 °F
DSC
Electrical Properties Metric English Comments
Dielectric Constant 3.18

@Frequency 1.00e+6 Hz
3.18

@Frequency 1.00e+6 Hz
ASTM D150
3.21

@Frequency 60.0 Hz
3.21

@Frequency 60.0 Hz
ASTM D150
3.23

@Frequency 1000 Hz
3.23

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 180 kV/mm

@Thickness 0.0500 mm
4570 kV/in

@Thickness 0.00197 in
Amorphous Film; ASTM D149
Dissipation Factor 0.0010

@Frequency 1000 Hz
0.0010

@Frequency 1000 Hz
ASTM D150
0.0020

@Frequency 60.0 Hz
0.0020

@Frequency 60.0 Hz
ASTM D150
0.0060

@Frequency 1.00e+6 Hz
0.0060

@Frequency 1.00e+6 Hz
ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 366 °C
691 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Melt Temperature 382 - 404 °C
720 - 759 °F
Mold Temperature 166 - 193 °C
331 - 379 °F
Drying Temperature 149 °C

@Time 14400 sec
300 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Natural
Form Pellets
Injection Rate Fast
Processing Technique Extrusion Blow Molding
Fiber (Spinning) Extrusion; Film Extrusion
Injection Blow Molding; Injection Molding
Machining; Profile Extrusion
Thermoforming; Wire & Cable Extrusion
Screw Compression Ratio 2.0:1.0 to 3.0:1.0