Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.40 GPa | 203 ksi | Tangent; 1.3 mm/min; ASTM D790 |
Mytex Polymers AS33L(W)-06 Polypropylene, Rubber modified, Talc filled, Compounded Description: AS33L(W)-06 is a compounded, talc, rubber modified polypropylene for exterior automotive applications. Material has outstanding moldability and excellent balance of high stiffness and .. |
|||
Flexural Modulus | >= 1.40 GPa | >= 203 ksi | ASTM D790 |
NIZHNEKAMSKNEFTEKHIM PP 1500J (T30G) Propylene Homopolymer Product obtained by polymerization of propylene in presence of complex metalorganic catalysts. It incorporates increased long-term thermal stability, thermal-oxidative degradation resistance when P.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
SABIC Innovative Plastics LNP FARADEX MS002 PP LNP* FARADEX* MS002 is a compound based on Polypropylene resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding. |
|||
Flexural Modulus | 1.40 - 14.0653 GPa @Temperature -40.0 - 120 °C |
203 - 2040.03 ksi @Temperature -40.0 - 248 °F |
Average value: 6.70 GPa Grade Count:3 |
Overview of materials for High Density Polyethylene (HDPE), Glass fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Glass fiber Filled". Each property range of values reported is minimum.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | 1% secant at 0.05 in/min; ASTM D790A |
LyondellBasell Astryn BA66K Polypropylene Copolymer, Flame Retardant Key Features: high melt flow, medium modulus, flame retardant polypropylene copolymer, high limiting oxygen index, non-halogenated, good aesthetics, excellent processabilityApplications: batteries, .. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | 1% Secant, 0.05 in/min; ASTM D790 |
LyondellBasell Hifaxâ„¢ AA56H Polypropylene Homopolymer Description: Hifaxâ„¢ AA56H medium high melt flow, 1,400 MPa flexural modulus, UL 94 V-2 flame retardant polypropylene homopolymer resin has an excellent combination of properties and processabil.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | 2 mm/min, 64mm span; ISO 178 |
SABIC Innovative Plastics SABIC PPCOMPOUND 7450 PP SABIC® PPcompound 7450 is a mineral filled, impact modified polypropylene TPO. This material can exhibit high impact resistance and good paintability in automotive exterior applications. The IMDS.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | DIN 53457 |
Schwartz Technical Plastics LAMIGAMID® 100 Polyamide 6, Extruded, Conditioned Application: machine parts under 80 mm diameter, hammer-heads, cup-shaped bearing shellsInformation provided by Schwartz Technical Plastics GmbH |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | 5 mm/min; GOST 9550 |
Sibur H250 GP Polypropylene Homopolymer Polypropylene homopolymer with narrow molecular weight distribution. It features high fluidity, an optimal stabilization package and balanced physical and mechanical properties.general purpose produ.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
Styrolution Styrolux® 693 D SBC Description: Styrolux® 693 D is a clear styrene-butadiene copolymer (SBC) with a well balanced combination of toughness and clarity. Styrolux® 693 D is mainly used for thermoformed articles, e.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF R1000I PA 66 High Impact Nylon 66 compound containing Impact Modifier. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOTUF R1000I PA 66 (Asia Pacific) High Impact Nylon 66 compound containing Impact Modifier. |
|||
Flexural Modulus | 1.40 GPa @Temperature 260 °C |
203 ksi @Temperature 500 °F |
ASTM D790 |
Saint-Gobain Meldin® 7001 Direct Formed Polyimide Finished parts and basic shapes made from unfilled polyimide material for structural applications requiring requiring high electrical insulative properties, high purity and low outgassing, and high .. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
UBE UBESTA® 3020X8 Nylon 12 Thermister Description: UBESTA Nylon 12 ThermisterInformation provided by UBE. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | 5mm/min; ISO 178 |
Borealis HB601WG Polypropylene Homopolymer HB601WG is a polypropylene homopolymer intended for injection molding and blow molding. The product is available in natural but other colors can be provided on request. This material has excellent .. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM-D790 |
Polyram RamLloy PVB101 ABS/NYLON alloy, Impact Modified Impact modified ABS/NYLON alloy for injection molding applicationsInformation provided by Polyram Ram On Ind. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
A. Schulman POLYFORT™ FPP 3708U UV Stable Copolymer Polypropylene DescriptionPolyfort® FPP 3708U is a 20% CAC03 filled UV stable copolymer polypropylene.Information provided by A. Schulman. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
Polyram RamShine PS580 High Impact Polystyrene, Flame Retardant Flame retardant V-0, high impact polystyrene for injection molding applications.Information provided by Polyram. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
Total HDPE SB 1461 High Density Polyethylene - Injection Stretch Blow Molding HDPE SB 1461 is a high density polyethylene with very high stiffness. It has been specifically designed for the manufacture of thin walled containers for foodstuffs (dairy applications particularly.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
Total PPH 3576 BB Polypropylene Homopolymer, Cast Film Polypropylene 3576 BB is recommended for use in non-oriented cast films processes. It contains an optimized level of slip and anti-block additives.3576 BB is intended for food, magazine or textile .. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | At 2 mm/min; ISO 178 |
Borealis Xmod™ PC75 High Crystalline Polypropylene Copolymer Xmod PC75 is a HCPP intended for injection molding of automotive interior parts. Xmod PC75 is a very easy-flowing material combined with a good balance between impact strength and stiffness. The m.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
Aclo Accuguard Polypropylene HP1362V2CSL Homopolymer Flame Retardant Copper Stabilized |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
Carmel Olefins CAPILENE® E 50 E Polypropylene Homopolymer CAPILENE® E 50 E is a low melt flow rate polypropylene homopolymer intended for extrusion, thermoforming and blow molding featuring very good process ability and melt stability. Products manufactur.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
Aclo Accucomp Polypropylene HPO306L Homopolymer |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | SAE J949 |
Azdel SuperLite® SL551600-100 PP Resin Matrix / 55% Glass Fiber (4 mm Molded Thickness) AZDEL SuperLite® SL551600-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
Braskem H 152 Fiber Extrusion Polypropylene Applications: Nonwoven by blow process for disposable diapers, personal care and disposable medical care. Information provided by Braskem |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ISO 178 |
Ascend Performance Materials Vydyne® M344 BLK Nylon 66, Flame Retardant, Conditioned Vydyne® M344 BLK is a halogenated, unfilled, flame-retardant PA66/6 copolymer designed with excellent strength and toughness. It is lubricated for machine feed and easy mold release and has Underwr.. |
|||
Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
Buckeye Polymers BP RPP 1010 TR Blk Reprocessed Polypropylene, 10% Mineral Filled Talc Filled BlackThis reprocessed product is successful in applications where cost is a major specification, yet physical characteristics require product performance. Industrial recycled resin comp.. |