Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.600 GPa @Temperature 90.0 °C |
87.0 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilamid B3N Unfilled, Nucleated PA6 Description: Nilamid B3N is an unfilled, nucleated NYLON 6. It is fast cycling, and combines ease of processing with good overall mechanical characteristics.Key characteristics: Fast cyclingEasy pro.. |
|||
Flexural Modulus | 0.600 GPa @Temperature 90.0 °C |
87.0 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
Nilit Nilitop BT FR C3 Unfilled, Flame Retardant PBT Description: Nilitop BT FR C3 is an unfilled, flame retardant PBT with halogens. The flame retardant does not contain PBB and PBDE, so it is compliant with the WEEE directive.Key characteristics: Go.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Reliance Industries Relene S42005 Polyethylene Wire and cable High Density Polyethylene grade. Characteristics: excellent processing, superior physical/electrical properties, good environmental stress crack resistance. Applications: recommended .. |
|||
Flexural Modulus | 0.600 GPa @Temperature 175 °C |
87.0 ksi @Temperature 347 °F |
ISO 178 |
Solvay Specialty Polymers Amodel® AP-9240 NL Polyphthalamide (PPA) Resin, 40% Mineral Filled, Dry as Molded
( AMODEL AP-9240 NL resin is a 40% mineral-filled, impact-modified polyphthalamide (PPA). It was designed to provide a smooth molded surface suitable for many decorative applications. This resin offer.. |
|||
Flexural Modulus | 0.600 - 4.30 GPa @Temperature -40.0 - 90.0 °C |
87.0 - 624 ksi @Temperature -40.0 - 194 °F |
Average value: 1.92 GPa Grade Count:4 |
Overview of materials for Nylon 66, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Unreinforced". Each property range of values reported is minimum and maximum values of appropr.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 1.3 mm/min; ASTM D790 |
ICO Polymers ICORENEâ„¢ 110-1332 LMDPE Rotational Molding Resin Description: ICORENE 110-1332 is a linear medium density polyethylene developed for use in rotational molding. This is a very fast processing material that quickly molds out to offer low surface po.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D747 |
Ineos B50-35H-011 HDPE Ineos B50-35H-011 is a high density polyethylene copolymer developed for blow molding applications. It is recommended for use in applications which require a combination of high top load strength a.. |
|||
Flexural Modulus | 0.600 - 0.700 GPa | 87.0 - 102 ksi | |
Isoflon Virgin PTFE Polytetrafluoroethylene Properties/Improved compression and wear resistanceExcellent chemical stabilityBetter thermal conductivityExcellent resistance to continuous service temperatures up to 260°C, and, for limited per.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Guarniflon MFA Fluoropolymer It’s a semi-crystalline fully-fluorinated melt processable fluoropolymer which offer the highest temperature rating and broadest chemical resistance of all melt processable fluoropolymers. It .. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | At 2 mm/min; ASTM D790 |
Borealis Borecene™ RM8343PL Linear Polyethylene for Rotational Molding Borecene RM8343PL is plasma treated linear medium density natural polyethylene for rotational molding with improved adhesion properties. The material is plasma treated to change the chemical struct.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 50% humidity; ISO 178 |
Borealis Borseal™ RE239CF Polypropylene Copolymer Borseal™ RE239CF is a random copolymer. This grade is suitable for the manufacturing of unoriented films for metallization. Applications: Borseal™ RE239CF is recommended for food packaging, high.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Borealis Borstar® ME6053 Black Bimodal MD Polyethylene Compound for Jacketing of Communication and Power Cables Borstar ME6053 is a natural, bimodal medium-density polyethylene compound produced using the Borstar process. It is characterized by its tailor made properties important in jacketing applications, .. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
Unipetrol PE HD LITEN® FB/FL 20 HDPE Made for tubular film and special applications.Information provided by Unipetrol RPA |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D 790 |
Total Lumicene® M 3410 EP HDPE Film, sheet FINACENE® M 3410 EP is a medium density metallocene based polyethylene resin. FINACENE® M 3410 EP is especially dedicated to film applications where a higher rigidity, good transparency and shrink.. |
|||
Flexural Modulus | 0.600 GPa @Temperature 80.0 °C |
87.0 ksi @Temperature 176 °F |
ASTM D790 |
Toyobo T-661 Nylon 66, Standard Grade (Conditioned) Features: Non-reinforced, Standard GradeInformation provided by Toyobo. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D 790 |
Total Lumicene® mPE M 3410 EP HDPE Film Outstanding clarity and gloss; excellent bubble stability; excellent tear strength; high puncture resistance; good stiffness; excellent heat sealing properties; excellent compatibility with LDPE and.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Covestro Bayflex® 110-80 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and o.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | cond; ISO 178 |
DSM Novamid® ST220 NAT PA6-I Impact Modified, Injection Molding, Medium Viscosity |
|||
Flexural Modulus | 0.600 GPa @Temperature 160 °C |
87.0 ksi @Temperature 320 °F |
ISO 178 |
DSM Stanyl® TW341-B PA46 Heat Stabilized, Lubricated |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 1% secant; ASTM D790 |
ExxonMobil LL 8360.29 Rotational Molding Resin Product Description: LL 8360 is a linear low density hexene copolymer designed to offer excellent processability along with outstanding dimensional control and low warpage. This resin is ideally sui.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | 1% secant; ASTM D790 |
ExxonMobil LLP8360.29 Rotational Molding Resin Product Description: LL 8360 is a linear low density hexene copolymer designed to offer excellent processability along with outstanding dimensional control and low warpage. This resin is ideally sui.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Buckeye Polymers BP Flex D5606 TPO TPO's are a family of thermoplastic elastomers which exhibit rubber-like properties and are processable on conventional thermoplastic equipment. These resins have excellent UV resistance and have a.. |
|||
Flexural Modulus | 0.600 GPa @Temperature 65.0 °C |
87.0 ksi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® 8202C HS PA6 (Dry) Ultramid 8202C HS is a heat stabilized, low viscosity, PA6 injection molding homopolymer possessing a modified crystalline structure for increased property performance and faster cycles. It is also.. |
|||
Flexural Modulus | 0.600 GPa @Temperature 65.0 °C |
87.0 ksi @Temperature 149 °F |
ASTM Test |
BASF Ultramid® 8202C PA6 (Dry) Ultramid 8202C is a modified crystalline and low viscosity, nylon 6 injection molding homopolymer. It is also available in heat stabilized (Ultamid 8202C HS) and/or pigmented versions. Its unique .. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
Chem Polymer Chemlon 256 Nylon 6, Wire Jacketing Grade A non-halogenated, Allwires rated wire coating grade used primarily on cables for power and control circuits in commercial and industrial applications. The cables are oil, gasoline, and abrasion re.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ASTM D790 |
3M Dyneon™ PFA FLEX 8502 UHPZ Perfluoroalkoxy Fluorothermoplastic Granules Dyneon™ PFA-FLEX UHP family exhibits improved environmental stress crack resistance to stress cracking agents such as fluorsurfactants and fluorosurfactant-containing chemicals. In addition, this f.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | SAE J949 |
Azdel SuperLite® SL551400-100 PP Resin Matrix / 55% Glass Fiber (6 mm Molded Thickness) AZDEL SuperLite® SL551400-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
Flexural Modulus | 0.600 - 1.15 GPa | 87.0 - 167 ksi | Average value: 0.875 GPa Grade Count:30 |
Overview of materials for High Density Polyethylene (HDPE), Rotational Molding Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Rotational Molding Grade". Each property range of values reported is m.. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | ISO 178 |
Unitika EX-1030 PA6, Conditioned High-impact nylonInformation provided by Unitika Ltd. |
|||
Flexural Modulus | 0.600 GPa | 87.0 ksi | |
Kraton® D1102 + PP blend (50/50) Unmodified polypropylene has high rigidity and good heat resistance, but poor impact resistance, especially at low temperatures. Blending KRATON D and G polymers with PP significantly improves the .. |