Teijin Multilon DN-3520F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon DN-3520F Filler Reinforced Type, Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It has improved stiffness through the addition of 20 % filler. Improved stiffness and high flowability realizes a thin wall of OA machines etc..Applications:Thin wall components of mechanical, electric and electronic equipment that need least warpage and dimensional accuracy etc.Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 4.00 mm |
0.0030 - 0.0050 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 58.0 MPa | 8410 psi | 50mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 50mm/min; ISO 527 |
| Tensile Modulus | 6.10 GPa | 885 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 5.40 GPa | 783 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm² | 28.6 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C @Temperature 20.0 °C |
16.7 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature 20.0 °C |
36.1 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | ISO 75 |
| Vicat Softening Point | 106 °C | 223 °F | 50°C/hr, 50N; ISO 306 |
| Flammability, UL94 | V-1 @Thickness 1.00 mm |
V-1 @Thickness 0.0394 in |
|
| V-0 @Thickness 1.30 mm |
V-0 @Thickness 0.0512 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Resin Technology Group 1105 Oxy-Bond™ Two-Component Epoxy Adhesive
- SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Europe-Africa-Middle East)
- Techmer ES HiFill FR® ABS FR V2 BK
- Saint-Gobain Norton® T-100 Virgin Skived PTFE Film (0.010" thick)
- ConocoPhillips ANDEROL® Assembly Lube Premium Quality White Mineral Oil Food Grade Grease, NLGI 1.5
- Buckeye Polymers BP ABS 8336 P ABS
- AFE Technologies Cronite Standard Nickel Alloy Castings, No. HR4
- PolyOne Edgetek® PI-20CF/000 Polyetherimide (PEI), Carbon Fiber Reinforced (discontinued **)
- Overview of materials for Thermoset Polyurethane, Elastomer, Glass Filled
Copyright © lookpolymers.com All Rights Reserved