Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.40 GPa | 783 ksi | STN EN ISO 178 |
Plastcom SLOVAMID 66 GF 10 GB 20 Polyamide 66, 10% Glass Fiber, 20% Glass Beads FeaturesPA 66 chemically reinforced with 10% glass fiber and with the content of 20% glass beads. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical properties can .. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | STN EN ISO 178 |
Plastcom SLOVASTER® B GF 20 Polybutylene Terephthalate, 20% Glass Fiber FeaturesPBT for injection moulding, chemically reinforced with 20% glass fiber. Characterized by excellent properties also at low temperatures like tensile and flexural modulus, tensile strength, a.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | |
Plastcom SLOVASTER® B1 HML GF 20 PBT, 20% glass fibre FeaturesPBT for injection moulding, chemically reinforced with 20% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 1.3 mm/min; ASTM D790 |
Ovation Polymers RIGITRON 10020 GF Polycarbonate, 20% Glass Reinforced PC - Glass reinforced (20 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. All samples are prepared accor.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics Cycoloy® C4220K PC+ABS (Asia Pacific) Cycoloy* C4220K resin is an injection moldable 20% glass reinforced non FR PC-ABS.
Key features include improved Knit Line strength, good flow, excellent strength & rigidity, heat resistance & hyd.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ISO 178 |
Nilit FRIANYL B63 SG-GV20 Nylon 6 for injection molding, 20% glass fiber reinforced Nylon 6 for injection molding, light impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | Longitudinal |
Quadrant Plastic Composites MultiQ® Impact Thermoplastic Panel Composite MultiQ is a product line of thermoplastic composites in panel form whose specific properties make them particularly suitable as an environmental alternative to plywood in outdoor applications. Howev.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D790 |
Parker Chomerics PREMIER™ A220-ST EMI Shielding Plastic Description: PREMIER™ is the world’s first and most versatile commercially available conductive thermoplastic for real world EMI shielding solutions. It is a blend of PC/ABS thermoplastic polymer .. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ISO 178 |
SABIC Innovative Plastics LNP Faradex EX06464 PEI (Asia Pacific) LNP* Faradex* EX06464 is a compound based on Polyetherimide resin containing Stainless Steel. Added features of this material include: Electrically
Conductive, EMI/RFI Shielding.This data was suppli.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP CG006 PS (Europe-Africa-Middle East) LNP* Lubricomp* CG006 is a compound based on Polystyrene resin containing Graphite. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2mm/min; ASTM D790 |
Kingfa JH720 G15 15% Glass Fiber Reinforced PC Features:Excellent balance propertiesHigh mechanical propertiesHigh stiffnessGood size stabilityGood surfaceApplications:Imaging equipment shellOA body frameElectrical equipmentComputer plug partsIn.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | d.a.m., 2 mm/min; ISO 178-A |
Lanxess Durethan® DP 2-2240/15 H2.0 901510 Nylon 66, 15% Glass Fiber PA 66, 15% glass fibers, blow molding, heat-aging stabilized, hydrolysis stabilizedInformation provided by LANXESS. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KP004L Acetal Copoly (Asia Pacific) LNP* Lubricomp* KP004L is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP KZL16 Acetal Copolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KZL16 is a compound based on Acetal Copolymer resin containing milled Glass and PTFE. Added features include; Internally Lubricated. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D 790 |
SABIC Innovative Plastics Valox® AB9515 ABS+PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Valox® DR48 PBT (Europe-Africa-Middle East) VALOX DR48 is a 17% glass reinforced, flame retardant injection moulding PBT resin. Applications: lamp sockets, connectors, switches, electrical housings and bases, bobbins, trimmers and electromoto.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP AF004L ABS LNP* THERMOCOMP* AF004L is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Low Extractible. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP KF002 Acetal Copolymer LNP THERMOCOMP* KF002 is a compound based on Acetal Copolymer resin containing 10% Glass Fiber. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL GFN2 PPE+HIPS (Asia Pacific) PPE+PS blend. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including pump.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL IGN5531 PPE+PS Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics NORYL IGN5531 PPE+PS (Asia Pacific) Noryl* IGN5531 is an 20% glass fiber reinforced, injection moldable grade. This modified polyphenylene ether resin is designed to deliver a balance of heat, strength and electrical properties. Nor.. |
|||
Flexural Modulus | 5.40 GPa @Temperature -40.0 °C |
783 ksi @Temperature -40.0 °F |
ASTM D790 |
Toyobo NB-5620S Nylon/Olefin Alloy, 15% Mineral Reinforced (Conditioned) Features: 15% Mineral Reinforced, Light WeightInformation provided by Toyobo. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D790 |
E-Polymers TEKAMID® TB110M40 , 40% Mineral Filled PA6, DAM 40% Mineral filled, Heat resistance, PlatableInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D790 |
E-Polymers TEKANATE™ G720 , 20% Glass Fiber Reinforced Poly Carbonate 20% Glass Fiber reinforcedInformation provided by E-Polymers Co. Ltd. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ISO 178 |
Ecomass® 705ZC75 Stainless Steel Filled ABS Nontoxic Alternative to traditional metals, weighting and balancing applicationsModerate Specific GravityStainless Steel Powder Filled ABSInformation provided by Technical Polymers |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | 2mm/min; ISO 178 |
Teijin Panlite® G-3420R Glass Fiber Reinforced Polycarbonate Resin GF 20% reinforced and mold release grade, meeting UL 94 V-2.Applications:Mechanical, electric and electronic components that need mechanical property e.g., stiffnessPrecision machinery components th.. |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D790 |
Aclo Accutech SAN SAN930G10L Glass Reinforced |
|||
Flexural Modulus | 5.40 GPa | 783 ksi | ISO 178 |
BASF Ultramid® B3WG3 15% Glass Filled PA6 (Dry) Description: Ultramid B3WG3 is a 15% glass fiber reinforced, heat stabilized injection molding PA6 grade.Information provided by BASF |