LATI Latiohm 82-02 PD09 PA12

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	LATI
Trade Name	Latiohm
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latiohm 82-02 PD09 PA12.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Semiconductive/dissipative product based on Polyamide 12 (PA12). Unfilled. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.22 g/cc	0.0441 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0090 - 0.011 cm/cm	0.0090 - 0.011 in/in
Linear Mold Shrinkage, Transverse	0.0090 - 0.012 cm/cm	0.0090 - 0.012 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	45.0 MPa	6530 psi
Elongation at Break	50 %	50 %
Elongation at Yield	15 %	15 %
Tensile Modulus	2.10 GPa	305 ksi
Charpy Impact Unnotched	2.50 J/cmÂ²	11.9 ft-lb/inÂ²
Charpy Impact, Notched	0.250 J/cmÂ²	1.19 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	115 Â°C	239 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	50.0 Â°C	122 Â°F
Vicat Softening Point	140 Â°C @Load 5.00 kg	284 Â°F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Surface Resistance	50 ohm	50 ohm

Processing Properties	Metric	English
Melt Temperature	210 - 240 Â°C	410 - 464 Â°F
Mold Temperature	45.0 - 60.0 Â°C	113 - 140 Â°F
Drying Temperature	80.0 - 100 Â°C @Time 10800 sec	176 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa

Users viewing this material also viewed the following: