Styron CALIBREâ„¢ 893-10 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name CALIBRE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron CALIBREâ„¢ 893-10 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CALIBREâ„¢ 893-10 resin provides superior ignition resistance in opaque applications. Applications: Portable/cellular phones Pagers Data Enclosures Computer housings, keyboards Structural components Business equipment Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Water Absorption 0.15 %
0.15 %
23°C, 24hrs; ASTM D570
Water Absorption at Saturation 0.32 %
0.32 %
23°C, 50% RH; ASTM D570
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 59
59
ASTM D785
Hardness, Rockwell R 123
123
ASTM D785
Tensile Strength, Ultimate 58.6 MPa
8500 psi
50 mm/min; ASTM D638
Tensile Strength, Yield 61.4 MPa
8900 psi
50 mm/min; ASTM D638
Elongation at Break 115 %
115 %
50 mm/min; ASTM D638
Tensile Modulus 2.38 GPa
345 ksi
50 mm/min; ASTM D638
Flexural Strength 97.9 MPa
14200 psi
3-points, 2 mm/min; ASTM D790
Flexural Modulus 2.33 GPa
338 ksi
3-points, 2 mm/min; ASTM D790
Izod Impact, Notched 6.94 J/cm
13.0 ft-lb/in
ASTM D256
Tensile Impact 160 J/cm
300 ft-lb/in
ASTM D1822
Dart Drop, Total Energy 62.0 J
45.7 ft-lb
8000 ipm; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 64.8 µm/m-°C

@Temperature -40.0 - 82.2 °C
36.0 µin/in-°F

@Temperature -40.0 - 180 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 137 °C
279 °F
annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
260 °F
annealed; ASTM D648
Vicat Softening Point 151 °C
304 °F
50°C/hr, 50N; ASTM D1525
Flammability, UL94 V-0
V-0
0.0625 in
V-0
V-0
0.125 in
Oxygen Index 36 %
36 %
ISO 4589-2