Polymer Property : Flexural Strength = 14200 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Nilit FRIANYL A63 HH-KV15 Nylon 6.6 for injection molding, 15% glass ball reinforced
Nylon 6.6 for injection molding, heat and hydrolysis stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
LG Chemical LUCEL EC-610B Electrically Conductive POM, 10% Carbon Black Filled
LUCEL semi-crystalline acetal copolymer resins are produced by gas phase polymerization. LUCEL resins can be widely accepted as the replacement of thermosets, aluminum and zinc die-casts or other m..
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
Kolon KOPA® KN333NW High Impact Nylon 66
Impact -resistant, dimensional safetyApplications Wheel coversInformation provided by API-Kolon.
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
LG Chemical Lupox® GP-1006F General Purpose PBT, Unreinforced, Flame Retardant, Non-Bleed
LUPOX semi-crystalline thermoplastic PBT resins exhibit properties including high strength, rigidity and good resistance to fatigue and creep at elevated temperatures. Furthermore, LUPOX resins sho..
Flexural Strength 97.9 MPa
14200 psi
2.0 in/min; ASTM D790
LTL Color Compounds ColorFast® PC60 Polycarbonate
6 melt extrusion gradeAll information provided by LTL Color Compounders, Inc.
Flexural Strength 98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP IFL21 PA6.12
LNP LUBRICOMP* IFL21 is a compound based on Nylon 6/12 resin containing 5% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON DX04462C PC
LNP STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Clean Compounding System, Electrically Conductive.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON DX96717C PC
LNP STAT-KON* DX96717C is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Flame Retardant.
Flexural Strength 98.1 MPa
14200 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Infino® HR-8070 MPPE, Unreinforced
Information provided by Samsung Cheil Industries.
Flexural Strength 98.1 MPa
14200 psi
2.8 mm/min; ASTM D790
Samsung Cheil Industries Infino® HR-8070 MPPE, Unreinforced
Information provided by Samsung Cheil Industries.
Flexural Strength 97.9 MPa
14200 psi
Method I (3 point load), 2.0 mm/min; ISO 178; ASTM D790
Styron CALIBREâ„¢ 891-10 Polycarbonate Resin
Overview: CALIBREâ„¢ 891-10 Series provides superior ignition resistance in opaque applications. The CALIBRE 891-10 series products are available in 2 additive packages: CALIBRE 891: Mold release..
Flexural Strength 97.9 MPa
14200 psi
ASTM D790
Styron EMERGEâ„¢ 4800-10 Polycarbonate
EMERGEâ„¢ 4800-10 advanced resin provides superior ignition resistance in opaque, injection molding applications. Physical properties and process-ability are outstanding for this class of polyca..
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP STAT-KON DX04462C PC (Asia Pacific)
LNP* STAT-KON* DX04462C is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Clean Compounding System.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
SABIC Innovative Plastics LNP Thermocomp OF002A PPS (Asia Pacific)
LNP* Thermocomp* OF002A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Strength 98.0 MPa
14200 psi
ISO 178
Polyram RamTough PZ780 Polycarbonate, UV Stabilized
General purpose, UV stabilized polycarbonate for injection molding applications.Information provided by Polyram.
Flexural Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Covestro Makrolon® FU4007 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Furniture applications..
Flexural Strength 97.9 MPa
14200 psi
ASTM D790
Ensinger XP-133 Compression Molded PI Compound, 20% Carbon Fiber
The XP-130 is an amorphous high performance thermoplastic with high permanent temperature and creep resistance as well as excellent bearing and wear properties, excellent long term thermal stability..
Flexural Strength 98.1 MPa
14200 psi
ASTM D790
E-Polymers TEKAFIN® PH70G1 HIPP + 10% Glass Fiber Reinforced Scratch Resistance Compounded-PP
Modified PP: TEKAFIN is modified PP resins formulated with various fillers and modifiers. It has product lines for impact modified, glass fiber reinforced, inorganic filler reinforced and hybrids.I..
Flexural Strength 98.1 MPa
14200 psi
ASTM D790
E-Polymers TEKAPPO® J910 10% Glass Fiber Reinforced M-PPO
Modified PPO/PPE: TEKAPPO is a modified PPO/PPE, blending PPO with HIPS in order to improve HDT and processability. It displays various HDT range with halogen-free flammability, impact resistance a..
Flexural Strength 97.9 MPa
14200 psi
Abatron AboCast 8503-4/AboCure 8503-4 Colorless Epoxy
AboCast 8503-4/AboCure 8503-4 is a general purpose, moderate speed, colorless epoxy casting compound with low viscosity. It offers a convenient 2/1 ratio by volume and lends itself to casting of thi..
Flexural Strength 98.0 MPa

@Temperature 300 °C
14200 psi

@Temperature 572 °F
Advanced Ceramics ZEMAT® ACL 2090 - Zero Expansion Glass-Ceramic
“Zero Expansion” glass-ceramic is a transparent material now in production for applications requiring ultra-low thermal expansion. The primary crystal phase is a s-eucryptite (Li2OAl2O32SiO2) soli..
Flexural Strength 98.0 MPa
14200 psi
23°C, 50% RH; ASTM D790
Asahi Kasei Xyron® 340Z Modified Polyphenylene Ether
Flame RetardantInformation provided by Asahi Kasei
Flexural Strength 97.9 MPa
14200 psi
ASTM D790
Asahi Kasei Thermylene® P1-20FG-2703 20% Glass Fiber Reinforced, Impact Modified
Information provided by Asahi Thermofil
Flexural Strength 98.1 MPa
14200 psi
2.8mm/min; ASTM D790
Asia International Enterprise (Hong Kong) 3010F Polybutylene terephthalate
Information provided by Asia International Enterprise (Hong Kong) Ltd.
Flexural Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Covestro Makrolon® Rx1851 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices• Low..
Flexural Strength 98.0 MPa
14200 psi
ASTM D790M
DSM Somos® ProtoTherm™ 12110 Water-resistant resin for stereolithography, Thermal Postcure
DescriptionDSM Somos® 12110 is a liquid photopolymer that produces strong, high temperature tolerant, water-resistant parts. Parts created with Somos® 12110 have a cherry-red appearance which tur..
Flexural Strength 97.9 MPa
14200 psi
ASTM D790
Polymer Resources PPX-GP5 Modified PPO, General Purpose with HDT of 270 F  (Unverified Data**)
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Flexural Strength 98.0 MPa
14200 psi
ASTM D790
LG Chemical LUPOY SR-3108F High Flow Modified PC, 10% Mineral Fillers, High Reflectivity, Flame Retardant
Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive..