- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 127 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 127 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
| RheTech Products G13P100-01 13% Glass Fiber Reinforced Polypropylene, Black Applications: Interior trimAir ducts - distributionFuel filler pocketInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 101R PC (Europe-Africa-Middle East) LEXAN 101R is a high viscosity multi purpose grade and contains a release agent to ensure easy processing. LEXAN 101R is available in transparent, translucent and opaque colours. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
| Polymer Resources PC-GP3-D-[color]-5 Polycarbonate, FDA-compliant Feedstocks, High Flow Polycarbonate, FDA-compliant Feedstocks, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
| Polymer Resources PPX-FRG20 Modified-PPO, V-1 Flame Retardant, 20% Glass Reinforced Modified-Polyphenylene Oxide, V-1 Flame Retardant, 20% Glass ReinforcedFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing condu.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® FXE161R PC (Europe-Africa-Middle East) LEXAN FXE161R is a transparent/translucent medium viscosity grade for special effects with fluorescent appearance. Color package may affect performance. LEXAN FXE161R contains a release agent to ens.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| PTS Tristar® PC-10R-(14) 14 MFI Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® HPS4 PC (Europe-Africa-Middle East) Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI).EtO, steam, e-beam, and gamma sterilizable... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® IR2240 PC (Europe-Africa-Middle East) IR 2240 resin is a medium-low flow (MFR = 10 at 300?C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. Food contact approved |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® ML104R PC (Europe-Africa-Middle East) LEXAN ML104R is a high viscosity multi purpose grade. FDA food contact compliant in limited colors. Effective January 15th, 2007 this grade will no longer be supported with biocompatibility inform.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DL003 PC (Asia Pacific) LNP LUBRICOMP* DL003 is a compound based on Polycarbonate resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
| Polymer Resources PC-UV3-D Polycarbonate, UV-stabilized, High Flow Polycarbonate, UV-stabilized, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by P.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 950 PC (Europe-Africa-Middle East) LEXAN 950 is a high viscosity flame retardant grade, especially suitable for electrical applications. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| PTS Tristar® PC-10FR-(V8) 8 MFI Flame Retardant, UV Stabilized Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| PTS Tristar® PC-10R-(V18) 18 MFI UV Stabilized Polycarbonate With Release Information provided by Polymer Technology and Services, LLC (PTS). |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® FXG101 PC (Europe-Africa-Middle East) FXG101 is a Lexan PC Translucent Grade in our VisualFX Portfolio. The Grade was developed to meet the Aesthetic Differentiation requirements of today´s Customers. Color package may effect prope.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® FXG101R PC (Europe-Africa-Middle East) LEXAN FXG101R is a transparent/translucent high viscosity grade for special effects colors with a diamond sparkle appearance. Color package may affect performance.This data was supplied by SABIC-IP .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® FXM161R PC (Europe-Africa-Middle East) LEXAN FXM161R is a transparent/translucent medium viscosity grade for special effects colours with a metallic-luster appearance. Color package may affect performance.This data was supplied by SABIC-.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® HP6 PC Low/med flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI). EtO and steam sterilizable. Contains mo.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics PC0703R PC (Asia Pacific) PC0703R resin is a low flow (MFR = 7 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the extrusion market. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics PC0703R PC (Europe-Africa-Middle East) PC0703R resin is a low flow (MFR = 7 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the extrusion market. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Unannealed; ASTM Data |
| Styron CALIBRE™ 701 15 Polycarbonate, General Purpose CALIBRE® 701 series polycarbonate resins are a general purpose, transparent, ignition resistant grades equipped with a mold release package. The CALIBRE 701 series resins exhibit a high heat resi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| Samyang Trirex® 3000H Polycarbonate, Low-temperature Impact PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3000H is a low temperature impact grade.Applications: Mobile Phone Housing, high gloss.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | Unannealed; ASTM Data |
| Styron CALIBRE™ 891 20 Polycarbonate, General Purpose CALIBRE® 890 series polycarbonate resins are a general purpose, superior ignition resistant grade equipped with a mold release package. The CALIBRE 890 series resins exhibit a high heat resistanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PX0888 PPE+PS Unfilled, non-FR. Higher heat resistance than N110 (BOZ) and px0844 (USA). For automotive interiors. 250F (121C) DTUL. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ISO 75-1/-2 |
| Covestro Makrolon® DP1-1843* Polycarbonate ISO 7391-PC,RL,(,,)-09-9Developmental productMVR (300 °C/1.2 kg) 9.5 cm3/10 minMedium viscosityUV stabilizedRotomoldingAvailable in transparent and translucent colorsGlobe lightsAs of 1 September 2.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | Unannealed; ASTM D648 |
| Entec Hylex® P1025L2 HB Polycarbonate Available in North America Additive: Mold Release Features: Good Mold Release and High Flow RoHS Compliant Form: Pellets Appearance: Blue Information provided by Entec |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| Ashley Polymers Ashlene® RH190H2-B Acetal General purpose, reprocessed homopolymer, excellent toughness, strength, stiffness and lubricity. UV stabilized with carbon black for outstanding weatherability.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | |
| BCC Products BC 4570 Polyester Hi Heat Filler BC 4570 is a multi-purpose paste designed for making quick repairs to a variety of substrates where service temperature exceeds 200º F (93º C). It is easy to mix and apply, cures in 15-20 minutes .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 261 °F | ASTM D648 |
| LATI LARIL 13 G/30 30% Glass Fiber Reinforced Polyphenylene Oxide (PPOm)
(Unverified Data**) Description: Laril thermoplastics are polyphenylene oxide (PPOm) products. They exhibit excellent toughness, even at low temperatures, good thermal resistance and dimensional stability are the most .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL FE1410PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1410PW resin is a blend of polyphenylene Oxide (PPO) and polystyrene (PS) resin that contains 10% glass reinforcement. The resin is suitable for injection molding. Noryl FE1410PW resin has .. |
|||