Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
RheTech Products G13P100-01UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, Black Applications: Interior trimAir ducts - distributionFuel filler pocketInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | 0.125 in bar; ASTM D648 |
Network Polymers PC-1029 Description: Natural PolycarbonateInformation provided by Network Polymers Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Polymer Resources PC-FD3 Polycarbonate, FDA-compliant Feedstocks, High Flow, Gamma Resistant Polycarbonate, FDA-compliant Feedstocks, High Flow, Gamma ResistantProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test sampl.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Polymer Resources PPX-FRG10 Modified-PPO, V-1 Flame Retardant, 10% Glass Reinforced Modified-Polyphenylene Oxide, V-1 Flame Retardant, 10% Glass ReinforcedFeatures: • Bromine Free • Chlorine FreeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing condu.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Polymer Resources PPX-GP5 Modified-PPO, General Purpose Modified-Polyphenylene Oxide, General Purpose, 270F HDTProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Informati.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Polymer Resources PPX-FRG20 Modified PPO, UL 94 V-1, 20% Glass Reinforced
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed, .125in; ASTM D648 |
Star Plastics PC1212FRR Molding Grade PC FR Information provided by Star Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed, .125in; ASTM D648 |
Star Plastics PC20NBR Molding Grade PC with Release Information provided by Star Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed, .125in; ASTM D648 |
Star Plastics PC721HFR Molding Grade PC High Flow with Release Information provided by Star Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed; ASTM D648 |
Styron EMERGEâ„¢ 4610-10 Polycarbonate EMERGEâ„¢ PC 4610-10 advanced resin is formulated to deliver both outstanding clarity and enhanced ignition resistance while maintaining excellent physical properties and processability. Applica.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed; ASTM D648 |
Styron EMERGEâ„¢ 4630-10 Polycarbonate EMERGEâ„¢ PC 4630-10 advanced resin is formulated to supply both excellent ultraviolet stability and enhanced ignition resistance while maintaining excellent physical properties and processabilit.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed; ASTM D648 |
Styron EMERGEâ„¢ 4850-19 Polycarbonate EMERGEâ„¢ 4850-19 advanced resin provides superior ignition resistance and ultraviolet light resistance in opaque applications. It has an f1 rating by Underwriters Laboratories Inc. Physical pr.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed, .125in; ASTM D648 |
Star Plastics PC1212R Molding Grade PC with Release Information provided by Star Plastics, Inc. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | Unannealed, 0.125 in; ASTM D648 |
Styron CALIBREâ„¢ 201-15 Polycarbonate Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | annealed; ASTM D648 |
Styron CALIBREâ„¢ 893-10 Polycarbonate CALIBREâ„¢ 893-10 resin provides superior ignition resistance in opaque applications. Applications: Portable/cellular phones Pagers Data Enclosures Computer housings, keyboards Structural compo.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | 0.157 in, unannealed; ASTM D648 |
Styron EMERGEâ„¢ 4310-15 Polycarbonate EMERGEâ„¢ PC 4310-15 advanced resin is high-performance polycarbonate resin offering high heat resistance and maximum toughness. Applications: Consumer Electronics and Information Technology Eq.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | unannealed; ASTM D648 |
Styron EMERGEâ„¢ 4800-7 Polycarbonate EMERGEâ„¢ 4800-7 advanced resin provides superior ignition resistance in opaque, injection molding applications. Physical properties and process-ability are outstanding for this class of polycar.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | annealed; ASTM D648 |
Lubrizol ISOPLAST™ 2560 Engineering Thermoplastic Polyurethane Resin for Medical Applications Features: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaAvailableInformation provided by LubrizolLubrizol acquired the Isoplast product line from Dow in 2009. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Chase Plastics CP Pryme® PC300HFR Polycarbonate (Utility Grade), High Flow, Mold Release Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Chase Plastics CP Pryme® PC300RUV Polycarbonate (Utility Grade), UV Stabilizer, Mold Release Information provided by Chase Plastics. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Clariant PCSP0014 GREY Polycarbonate, Stainless Steel Fiber, EMI Data provided by Clariant Masterbatches |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | Unannealed; ASTM D648 |
Entec Hylex® P1025L2 HB Polycarbonate Available in North America Additive: Mold Release Features: Good Mold Release and High Flow RoHS Compliant Form: Pellets Appearance: Blue Information provided by Entec |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | ASTM D648 |
Entec Hylex® P1325L1 HB Polycarbonate UV Stabilized, High Flow, Mold Release, Water ClearInformation provided by Entec. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | >= 127 °C | >= 260 °F | ISO 75 |
Bulk Molding Compounds BMC 665 Mineral filled, 20% glass reinforced polyester molding compound Description: BMC 665 molding compound is a mineral filled, glass reinforced polyester molding compound suitable for compression, transfer or stuffer injection molding. It is characterized by good.. |
|||
Deflection Temperature at 1.8 MPa (264 psi) | 127 °C | 260 °F | |
BCC Products BC 4570 Polyester Hi Heat Filler BC 4570 is a multi-purpose paste designed for making quick repairs to a variety of substrates where service temperature exceeds 200º F (93º C). It is easy to mix and apply, cures in 15-20 minutes .. |