SABIC Innovative Plastics Lexan® LCG0820 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® LCG0820 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D 792 |
| Water Absorption | 0.12 % @Time 86400 sec |
0.12 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 154 MPa | 22300 psi | SABIC - Japan Method |
| Elongation at Break | 4.0 - 6.0 % | 4.0 - 6.0 % | SABIC - Japan Method |
| Flexural Strength | 205 MPa | 29700 psi | ASTM D 790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.47 J/cm @Temperature 23.0 °C |
2.75 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 - 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.1 - 27.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| Deflection Temperature at 0.46 MPa (66 psi) | 142 °C @Thickness 3.20 mm |
288 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 - 1.00e+8 ohm | 1000 - 1.00e+8 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Nye Lubricants 368AX-F (RL) Synthetic Oil
- Owens Corning Glass Fiber Reinforced Polyurethane, Milled Fibers (RRIM), 13 wt.% glass
- Kolon SPESIN® KP212G15V0BM G/F Reinforced & Flame Retardant PBT Compound Resin
- Global GPP-2000 Polypropylene Impact Copolymer, Cold Temperature Impact Resistant, Nucleated
- Samsung Cheil Industries Starex® NH-0925U ABS, Unreinforced FR
- Wellman Wellamid® GF30-60 XE-NBK1 33% Glass Fiber Reinforced Nylon 6
- Elgiloy® Co-Cr-Ni Alloy, Wire, 65% Cold Reduction, Heat Treated
- Cadi 3 MOLD-MOR™
- A. Schulman ComAlloy Comtuf® 651 Nylon 6, Mineral Reinforced, Impact Modified
- Johnson Matthey JM Tenacity 2 Brazing Flux Powder
Copyright © lookpolymers.com All Rights Reserved