- Carpenter AerMet®-for-Tooling Tool Steel, Double Aged 468°C
Carpenter AerMet®-for-Tooling Tool Steel, Double Aged 468°C
| Category | Metal , Ferrous Metal , Tool Steel , Air-Hardening Steel |
| Manufacturer | Carpenter Technology Corporation (Cartech) |
| Trade Name | AerMet®-for-Tooling |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Carpenter AerMet®-for-Tooling Tool Steel, Double Aged 468°C.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Carpenter Technology Corporation.This is a double vacuum melted alloy with high hardness and strength combined with exceptional ductility and toughness. The alloy is designed for components which require a combination of HRC 53/55 hardness with the highest toughness available.AerMet® is a registered trademark of Carpenter Technology Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.892 g/cc | 0.2851 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 560 | 560 | Estimated from Rockwell C for 3000 kg load, 10 mm ball Brinell measurement. |
| Hardness, Knoop | 621 | 621 | Estimated from Rockwell C |
| Hardness, Rockwell C | 55 | 55 | |
| Hardness, Vickers | 594 | 594 | Estimated from Rockwell C |
| Tensile Strength, Ultimate | 2069 MPa | 300100 psi | |
| Tensile Strength, Yield | 1793 MPa @Strain 0.200 % |
260100 psi @Strain 0.200 % |
|
| Elongation at Break | 12 % | 12 % | |
| Reduction of Area | 60 % | 60 % | |
| Modulus of Elasticity | 194.4 GPa | 28200 ksi | Young's Modulus |
| Shear Strength | 1207 MPa | 175100 psi | |
| Charpy Impact | 27.0 J | 19.9 ft-lb | V-notch |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.99 µm/m-°C @Temperature 24.0 - 93.0 °C |
5.55 µin/in-°F @Temperature 75.2 - 199 °F |
|
| 10.8 µm/m-°C @Temperature 24.0 - 260 °C |
6.00 µin/in-°F @Temperature 75.2 - 500 °F |
||
| 11.57 µm/m-°C @Temperature 24.0 - 538 °C |
6.428 µin/in-°F @Temperature 75.2 - 1000 °F |
||
| Thermal Conductivity | 24.8 W/m-K @Temperature 25.0 °C |
172 BTU-in/hr-ft²-°F @Temperature 77.0 °F |
|
| 30.6 W/m-K @Temperature 200 °C |
212 BTU-in/hr-ft²-°F @Temperature 392 °F |
||
| 32.6 W/m-K @Temperature 400 °C |
226 BTU-in/hr-ft²-°F @Temperature 752 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.23 % | 0.23 % | |
| Chromium, Cr | 3.0 % | 3.0 % | |
| Cobalt, Co | 13.4 % | 13.4 % | |
| Iron, Fe | 71 % | 71 % | as remainder |
| Molybdenum, Mo | 1.2 % | 1.2 % | |
| Nickel, Ni | 11.1 % | 11.1 % |