Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH50
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® B 50H1 Nylon 66/6, Flame Retardant, EH50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant copolyamide 66/6, unreinforced, heat stabilized, for injection molding.This phosphorus and halogen free flame retardant grade, UL 94 VO (0.4 mm), offers excellent filling qualities and with good stiffness. It is particularly suitable for molding insulating parts for electrical components on board materials for use in tunnels, satisfying specification n°3 of the standard "Fire and Smoke" NF-F16102, and on components for electrical connections : junction blocks, terminal blocks, connectors.This product is available in natural, black, and in colors on request.Glow wire test thick. 1,6 mm: no flame, IEC 695-2-1, is 650°C. Glow wire test thick. 0,8 mm: c
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183-A |
| Water Absorption | 1.1 % | 1.1 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ISO 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO 527 |
| Elongation at Break | 100 % | 100 % | ISO 527 |
| Elongation at Yield | 13 % | 13 % | ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Izod Impact Resistance | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | NB | NB | ISO 179/EU-1993 |
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 242 °C | 468 °F | ISO 3146-C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243-1 |
| Dissipation Factor | 0.060 @Frequency 1e+6 Hz |
0.060 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 250 °C | 464 - 482 °F | |
| Middle Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Front Barrel Temperature | 250 - 260 °C | 482 - 500 °F |
Users viewing this material also viewed the following:
- RheTech Products FT1100-689UV Thermoplastic Polyolefin, UV Stabilized, Light Natural Beige
- Ineos ABS Centrex® 833 ASA+AES Blend (discontinued **)
- Global PP-1102-K Polypropylene Homopolymer
- LATI Latamid 66 B H-V0 PA 66, Heat Stabilized, Flame Retardant
- Styron Magnumâ„¢ 375 HP Acrylonitrile Butadiene Styrene (ABS)
- Silberline Sparkle Silver® Premier 572
- Dandong Taico Minerals TAICOCITE® TC50 Magnesium Hydroxide
- ArcelorMittal 260 BH Bake hardening steel, Cold rolled
- A. Schulman POLYFORT™ FPP 1427 Mineral Filled Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved