LATI Latamid 66 B H-V0 PA 66, Heat Stabilized, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized , Nylon 66, Unreinforced, Flame Retardant
Manufacturer LATI
Trade Name Latamid
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LATI Latamid 66 B H-V0 PA 66, Heat Stabilized, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide 66 (PA66) based compound. High fluidity. Heat stabilized. UL94 V-0 classified, halogens-based flame retardants and red phosphorous free. Blended with PA6.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
Linear Mold Shrinkage, Flow 0.0080 - 0.011 cm/cm
0.0080 - 0.011 in/in
Linear Mold Shrinkage, Transverse 0.0085 - 0.0115 cm/cm
0.0085 - 0.0115 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.0 MPa

@Temperature 60.0 °C
 7980 psi

@Temperature 140 °F
80.0 MPa

@Temperature 23.0 °C
 11600 psi

@Temperature 73.4 °F
Elongation at Break 8.0 %

@Temperature 23.0 °C
 8.0 %

@Temperature 73.4 °F
50 %

@Temperature 60.0 °C
 50 %

@Temperature 140 °F
>= 100 %

@Temperature 90.0 °C
 >= 100 %

@Temperature 194 °F
>= 100 %

@Temperature 120 °C
 >= 100 %

@Temperature 248 °F
>= 100 %

@Temperature 150 °C
 >= 100 %

@Temperature 302 °F
Elongation at Yield 4.0 %
4.0 %
Tensile Modulus 0.600 GPa

@Temperature 150 °C
 87.0 ksi

@Temperature 302 °F
0.800 GPa

@Temperature 120 °C
 116 ksi

@Temperature 248 °F
1.10 GPa

@Temperature 90.0 °C
 160 ksi

@Temperature 194 °F
1.80 GPa

@Temperature 60.0 °C
 261 ksi

@Temperature 140 °F
3.80 GPa

@Temperature 23.0 °C
 551 ksi

@Temperature 73.4 °F
Charpy Impact Unnotched 5.00 J/cm²

@Temperature -20.0 °C
 23.8 ft-lb/in²

@Temperature -4.00 °F
5.50 J/cm²

@Temperature 23.0 °C
 26.2 ft-lb/in²

@Temperature 73.4 °F
Charpy Impact, Notched 0.280 J/cm²

@Temperature -20.0 °C
 1.33 ft-lb/in²

@Temperature -4.00 °F
0.300 J/cm²

@Temperature 23.0 °C
 1.43 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 95.0 °C
203 °F
Deflection Temperature at 0.46 MPa (66 psi) 235 °C
455 °F
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Vicat Softening Point 240 °C

@Load 5.00 kg
 464 °F

@Load 11.0 lb
Flammability, UL94 V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Oxygen Index 32 %
32 %
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 GWFI/GWT
960 °C

@Thickness 2.00 mm
 1760 °F

@Thickness 0.0787 in
 GWFI/GWT
Electrical Properties Metric English Comments
Comparative Tracking Index 525 V
525 V
A solution
Processing Properties Metric English Comments
Melt Temperature 265 - 275 °C
509 - 527 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 90.0 - 100 °C

@Time 10800 sec
 194 - 212 °F

@Time 3.00 hour
Descriptive Properties Value Comments
ISO Shrinkage - Pressure 60 MPa