Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Amodel® AT-1001L Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Amodel AT-1001L is an unreinforced, impact modified polyphthalamide (PPA) resin that exhibits exceptional impact strength at temperatures ranging from room temperature to as low as -40°F (-40°C), which suggests possible applications in ski boots and hockey skates. In addition, its chemical and wear resistance, combined with good mechanical properties, make Amodel AT-1001L resin a prime candidate for applications such as anti-friction and wear resistant components, chemical, oil field, automotive and safety equipment. - Natural: AT-1001 L NTAdditional Information: Penetration Impact, ASTM D3763, 73°F, Maximum Load: 1100 lbs Penetration Impact, ASTM D3763, 73°F, Total Energy Absorbed: 40 ft-lbs Penetration Impact, ASTM D3763, 73°F, Energy to Maximum Load: 30 ft-lbs Penetration Impact, ASTM D3763, -10°F, Total Energy Absorbed: 40 ft-lbs Penetration Impact, ASTM D3763, -10°F, Maximum Load: 1260 lbs Penetration Impact, ASTM D3763, -10°F, Energy to Maximum Load: 30 ft-lbsData is presented for dry polymer.Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
ISO 1183/A
Water Absorption 0.75 %

@Time 86400 sec
0.75 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.017 - 0.019 cm/cm
0.017 - 0.019 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.019 - 0.021 cm/cm
0.019 - 0.021 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.1 MPa
9010 psi
ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
Tensile Modulus 1.90 GPa
276 ksi
ASTM D638
Flexural Strength 96.5 MPa
14000 psi
ASTM D790
Flexural Modulus 2.21 GPa
321 ksi
ASTM D790
Poissons Ratio 0.35
0.35
ASTM E132
Shear Modulus 0.704 GPa
102 ksi
Calculated
Izod Impact, Notched 7.50 J/cm

@Temperature -40.0 °C
14.1 ft-lb/in

@Temperature -40.0 °F
ASTM D256
11.0 J/cm

@Temperature 23.0 °C
20.6 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Melting Point 310 °C
590 °F
Deflection Temperature at 1.8 MPa (264 psi) 120 °C

@Thickness 3.18 mm
248 °F

@Thickness 0.125 in
Annealed; ASTM D648
Processing Properties Metric English Comments
Feed Temperature 79.4 °C
175 °F
Hopper Temperature
Rear Barrel Temperature 304 - 318 °C
579 - 604 °F
Front Barrel Temperature 316 - 329 °C
601 - 624 °F
Melt Temperature 321 - 343 °C
610 - 649 °F
Mold Temperature 65.6 - 110 °C
150 - 230 °F
Drying Temperature 110 °C
230 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.045 %
0.045 %
Descriptive Properties Value Comments
Additive Impact Modifier
Lubricant
Mold Release
Appearance Natural Color
Automotive Specifications ASTM D5336 PPA0110A01080 Color: NT Natural
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Ductile
Good Chemical Resistance
Good Wear Resistance
Hot Water Moldability
Impact Modified
Low Temperature Impact Resistance
Low Warpage
Lubricated
Forms Pellets
Generic PPA
Processing Method Injection Molding
Water-Heated Mold Injection Molding
Uses Automotive Applications
Automotive Electronics
General Purpose
Housings
Industrial Applications
Industrial Parts
Machine/Mechanical Parts
Metal Replacement
Oil/Gas Applications
Copyright © lookpolymers.com All Rights Reserved