- Polymer Property : Tensile Strength at Break = 62.1 MPa
Polymer Property : Tensile Strength at Break = 62.1 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9010 psi | Type I, 5.1 mm/min; ASTM D638 |
| PolyOne Nymax™ GBF 1010 35 BLACK 13 Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC/TP-GP3-G10 PC/Polyester Alloy, 10% Glass Reinforced Superior Chemical Resistance, 10% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP3-D Polycarbonate, General Purpose, High Flow Polycarbonate, General Purpose, High FlowFeatures: • High Impact Resistance • Self ExtinguishingProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inc.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP4-[color]-1 Polycarbonate, General Purpose, Easy Flow with Mold Release Polycarbonate, General Purpose, Easy Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Infor.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP4-[color]-5 Polycarbonate, FDA-compliant Feedstocks, Easy Flow Polycarbonate, FDA-compliant Feedstocks, Easy FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pr.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PC-GP4-[color]-6 Polycarbonate, FDA-compliant Feedstocks, Easy Flow with Mold Release Polycarbonate, FDA-compliant Feedstocks, Easy Flow with Mold ReleaseProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samp.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PPX-G5 Modified-PPO, 5% Glass Reinforced Modified-Polyphenylene Oxide, 5% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information pro.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Ravago Manufacturing Americas Hylon® N1040MHL Nylon 6/6 (Cond) Information provided by Ravago. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 301 TFE 5 FR L Polycarbonate (PC), Glass Fiber - PTFE Lubricated - Flame Retardant - Non-PBBO/E - UL94 V-0 The RTP 301 TFE FR L series of compounds incorporate various percentages of PTFE into a glass fiber reinforced polycarbonate base which also includes external lubricants for enhanced processing. Th.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 601 FR Acrylonitrile Butadiene Styrene (ABS), Glass Fiber - Flame Retardant - UL94 V-0 RTP 601 FR is a 10% glass fiber reinforced ABS compound. RTP 601 FR offers a favorable balance of physical properties, molding lattitudes, and ignition resistance. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 699 X 85843 Acrylonitrile Butadiene Styrene (ABS), Glass Fiber - Permanently Anti-static |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 800 AR 5 Acetal (POM), Aramid Fiber Reinforced |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources NY6-IM1 Nylon 6, Impact Modified Nylon 6, Impact ModifiedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources NY6-IM1-[color]-H Nylon 6, Impact Modified, Heat Stabilized Nylon 6, Impact Modified, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grad.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Techmer ES Plaslube® NY-1/TF/20 NAT PA66 |
|||
| Tensile Strength at Break | >= 62.1 MPa @Temperature 23.9 °C |
>= 9000 psi @Temperature 75.0 °F |
|
| Master Bond EP21ARHT Two component epoxy adhesive, sealant, coating and encapsulating system Product Description: Master Bond EP21ARHT is a two component epoxy resin system for high performance bonding, sealing, coating and encapsulating. It has a convenient 100 to 50 mix ratio by weight an.. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Chase Plastics CP Pryme® N110GL (COND, 50% RH) Nylon 6, 10% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Chase Plastics CP Pryme® PC310GR Polycarbonate (Utility Grade), 10% Glass Fiber Reinforced, Mold Release Information provided by Chase Plastics. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company EMI 330 C FR Polycarbonate (PC), Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection - Flame Retardant |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 1400 P TFE 10 Polyphenyl Sulfone (PPSU), PTFE Lubricated - Preliminary Data |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 2599 X 87260 B Polycarbonate/ABS Alloy (PC/ABS), Carbon Nanotube - ESD Protection - Static Dissipative |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 1300 C TFE 20 Polyphenylene Sulfide (PPS), PTFE Lubricated |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 200 D AR 10 TFE 5 Nylon 6/12 (PA), Aramid Fiber - PTFE Lubricated |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 200 TFE 18 SI 2 Nylon 6/6 (PA) PTFE Lubricated - Silicone Lubricated |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | |
| Abatron AboCast 8103-20 High-Performance Dielectric Epoxy AboCast 8103-20 is a dielectric in/outdoor epoxy system with superior arc-track resistance, high voltage and heat resistance, low ash and ion content, and it is chlorine-free. This system is unique .. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PPX-GP5 Modified PPO, General Purpose with HDT of 270 F
(Unverified Data**) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D638 |
| Polymer Resources PPX-MF-FR1 Modified PPO, UL 94 V-0 with HDT of 190 F, Mineral Reinforced
(Unverified Da Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation. |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| RTP Company RTP 399 X 86846 H Polycarbonate (PC) Flame Retardant - Halogen Free - Transparent |
|||
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |