SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific)

Category Polymer , Thermoplastic , ASA Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D 792
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.80 %

@Temperature 23.0 °C
0.80 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0030 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0030 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 2.0 g/10 min

@Load 5.00 kg,
Temperature 220 °C
2.0 g/10 min

@Load 11.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
9.7 g/10 min

@Load 10.0 kg,
Temperature 220 °C
9.7 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 26.0 MPa
3770 psi
50 mm/min; ISO 527
32.0 MPa
4640 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 36.0 MPa
5220 psi
Type I, 50 mm/min; ASTM D 638
36.0 MPa
5220 psi
50 mm/min; ISO 527
Elongation at Break 28 %
28 %
50 mm/min; ISO 527
38 %
38 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 3.4 %
3.4 %
Type I, 50 mm/min; ASTM D 638
3.4 %
3.4 %
50 mm/min; ISO 527
Tensile Modulus 1.79 GPa
260 ksi
1 mm/min; ISO 527
1.91 GPa
277 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 56.0 MPa
8120 psi
1.3 mm/min, 50 mm span; ASTM D 790
56.0 MPa
8120 psi
2 mm/min; ISO 178
Flexural Modulus 1.83 GPa
265 ksi
1.3 mm/min, 50 mm span; ASTM D 790
1.87 GPa
271 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.700 J/cm

@Temperature -30.0 °C
1.31 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
1.95 J/cm

@Temperature 23.0 °C
3.65 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -30.0 °C
3.33 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
13.0 kJ/m²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 28.0 J

@Temperature 23.0 °C
20.7 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 92.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
51.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
100 µm/m-°C

@Temperature -40.0 - 40.0 °C
55.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 109 µm/m-°C

@Temperature -40.0 - 40.0 °C
60.6 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
116 µm/m-°C

@Temperature -40.0 - 40.0 °C
64.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 71.0 °C
160 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
69.0 °C

@Thickness 3.20 mm
156 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 82.0 °C
180 °F
Rate B/50; ISO 306
85.0 °C
185 °F
Rate B/120; ISO 306
85.0 °C
185 °F
Rate B/50; ASTM D 1525