SABIC Innovative Plastics NORYL PX9406K PPE+HIPS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL PX9406K PPE+HIPS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL* PX9406K resin may be suitable for consumer electronics applications. Flame retardant used is non-halogenated. UL94 V0 at 1.5 mm, 5VB at 2 mm, and 5VA at 2.5 mm. RTI (impact) = 105 C
Physical Properties Metric English Comments
Specific Gravity 1.10 g/cc
1.10 g/cc
ASTM D792
Density 1.10 g/cc
0.0397 lb/in³
ISO 1183
Viscosity 250000 cP
250000 cP
Melt Viscosity, 280°C, 1500 sec-1; ISO 11443
390000 cP
390000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
525000 cP
525000 cP
Melt Viscosity, 250°C, 1500 sec-1; ISO 11443
Melt Index of Compound 7.0 g/10 min

@Load 10.0 kg,
Temperature 250 °C
7.0 g/10 min

@Load 22.0 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
11 g/10 min

@Load 5.00 kg,
Temperature 280 °C
11 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D638
52.0 MPa
7540 psi
50 mm/min; ISO 527
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
67.0 MPa
9720 psi
50 mm/min; ISO 527
Elongation at Break 45 %
45 %
Type I, 50 mm/min; ASTM D638
55 %
55 %
50 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
50 mm/min; ISO 527
5.7 %
5.7 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.55 GPa
370 ksi
1 mm/min; ISO 527
2.70 GPa
392 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
101 MPa
14600 psi
6.4 mm; ASTM D790
104 MPa
15100 psi
2 mm/min; ISO 178
Flexural Modulus 2.42 GPa
351 ksi
2 mm/min; ISO 178
2.65 GPa
384 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.65 GPa
384 ksi
6.4 mm; ASTM D790
Izod Impact, Notched 1.70 J/cm
3.18 ft-lb/in
ASTM D256
1.00 J/cm

@Temperature -30.0 °C
1.87 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.500 J/cm²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 55.0 J

@Temperature 23.0 °C
40.6 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 128 °C

@Thickness 3.20 mm
262 °F

@Thickness 0.126 in
unannealed; ASTM D648
130 °C

@Thickness 6.40 mm
266 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 111 °C
232 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
113 °C

@Thickness 3.20 mm
235 °F

@Thickness 0.126 in
unannealed; ASTM D648
121 °C

@Thickness 6.40 mm
250 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 134 °C
273 °F
Rate B/120; ISO 306
144 °C
291 °F
Rate A/120; ISO 306
UL RTI, Electrical 110 °C
230 °F
UL 746B
UL RTI, Mechanical with Impact 105 °C
221 °F
UL 746B
UL RTI, Mechanical without Impact 110 °C
230 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94 by SABIC-IP
5VA

@Thickness 2.50 mm
5VA

@Thickness 0.0984 in
UL 94 by SABIC-IP
Glow Wire Test 800 °C
1470 °F
IEC 60695-2-13
800 °C
1470 °F
IEC 60695-2-13
800 °C
1470 °F
IEC 60695-2-13
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.40e+17 ohm-cm
1.40e+17 ohm-cm
ASTM D257
Dielectric Strength 49.0 kV/mm

@Thickness 3.20 mm
1240 kV/in

@Thickness 0.126 in
in air; ASTM D149
Comparative Tracking Index 250 V
250 V
IEC 60112
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2