Polymer Property : Melt Index of Compound = 11 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Physical Properties Metric English Comments
Melt Index of Compound 11 g/10 min

@Load 1.20 kg,
Temperature 250 °C
11 g/10 min

@Load 2.65 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® LUX2910 PC (Asia Pacific)
Global grade. LEXAN LUX2910 is an injection moulding grade especially designed for manufacturing optical parts requiring superior flow properties combined with very high transmission and color stabi..
Melt Index of Compound 11 g/10 min

@Load 1.20 kg,
Temperature 250 °C
11 g/10 min

@Load 2.65 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® LUX2910T_ PC (Europe-Africa-Middle East)
Global grade. LEXAN LUX2910T is an injection moulding grade especially designed for manufacturing optical parts requiring superior flow properties combined with very high transmission and color stab..
Melt Index of Compound 11 g/10 min

@Load 2.16 kg,
Temperature 300 °C
11 g/10 min

@Load 4.76 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Lexan® EX1632T PC (Europe-Africa-Middle East)
LEXAN* EX1632T polycarbonate resin, MVR (300C/1.2kg) 6 cm3/10min, high viscosity, branched, extrusion, mold release, UV stabilized, transparent, translucent and opaque colors. Multiwall sheet, Profi..
Melt Index of Compound 11 g/10 min

@Load 5.00 kg,
Temperature 280 °C
11 g/10 min

@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics NORYL PX9406K PPE+HIPS (Asia Pacific)
NORYL* PX9406K resin may be suitable for consumer electronics applications. Flame retardant used is non-halogenated. UL94 V0 at 1.5 mm, 5VB at 2 mm, and 5VA at 2.5 mm. RTI (impact) = 105 C
Melt Index of Compound 11 g/10 min

@Load 5.00 kg,
Temperature 260 °C
11 g/10 min

@Load 11.0 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF0335 PC (Europe-Africa-Middle East)
LNP* Lubricomp* LEXAN_LF0335 compound is a 35% glass fiber, milled glass reinforced PC injection moulding resin with improved wear resistance and reduced friction.
Melt Index of Compound 11 g/10 min

@Load 1.20 kg,
Temperature 250 °C
11 g/10 min

@Load 2.65 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® 4012 PBT (Europe-Africa-Middle East)
VALOX 4012 is a 10% high strength glass fibre reinforced PBT injection moulding resin with improved mechanical properties. Applications: connectors.
Melt Index of Compound 11 g/10 min

@Load 2.16 kg,
Temperature 250 °C
11 g/10 min

@Load 4.76 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® 457 PBT (Europe-Africa-Middle East)
VALOX 457 is a 6.5% glass fibre reinforced flame retarded PBT injection moulding resin. Applications: electrical and appliances industries.
Melt Index of Compound 11 g/10 min

@Load 1.20 kg,
Temperature 265 °C
11 g/10 min

@Load 2.65 lb,
Temperature 509 °F
MVR [cm^3/10 min]; ISO 1133
SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East)
VALOX 855 is 15% glass reinforced PBT+PET blend with improved surface appearance. Applications: external housings, steam irons, appliance housings and lighting parts.
Melt Index of Compound 11 g/10 min

@Load 5.00 kg,
Temperature 250 °C
11 g/10 min

@Load 11.0 lb,
Temperature 482 °F
MVR [cm^3/10 min]; ASTM D1238
SABIC Innovative Plastics Valox® ENH8530 PBT+PET (Europe-Africa-Middle East)
Non-Brominated & Non-Chlorinated Flame Retardant, 15% Glass fiber reinforced PBT/PET blend