Polymer Property : Tensile Strength, Yield = 9570 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Cycoloy® CY6414 PC (Europe-Africa-Middle East)
Flame retardant modified PC blend using non-brominated and non-chlorinated flame retardant systems, offering high heat for application in appliances, lighting and electrical market.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Lexan® 4404 PPC+PC (Asia Pacific)
High heat polycarbonate copolymer, with HDT of 287F at 264 psi. FDA food contact compliant. Effective Jan 15th, 2008 this grade should not be used for medical applications which require biocompatibi..
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 503 PC
10% GR PC. Optimum combination of high modulus plus excellent impact strength and flame retardance. UV-stabilized.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 915AU PC
LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte..
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Lexan® 915AU PC (Asia Pacific)
LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® 915AU PC (Asia Pacific)
LEXAN resin grade 915AU is a flame retardant polycarbonate featuring non brominated and non chlorinated FR systems, with good flow, and good UV stability. It is available in transparent colors, inte..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® CFR7431 PC COPOLYMER (Asia Pacific)
Lexan* CFR7431 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm an..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Lexan® LUX7432C PC COPOLYMER (Europe-Africa-Middle East)
Lexan* LUX7432C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm a..
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics GELOY XTPMFR10 ASA+PC (Asia Pacific)
Improved ASA/PC blend for high flow, 1.0mm V0 applications. Improved UV performance aesthetically and physically compared to alternatives.
Tensile Strength, Yield 66.0 MPa
9570 psi
ISO 527
Premix Thermoplastics PRE-ELEC® 12-031  (discontinued **)
PRE-ELEC 12-031 is a conductive thermoplastic compound based on a polyacetal copolymer with 10% carbon fiber. PRE-ELEC 12-031 exhibits excellent mechanical properties and electrical conductivity. Te..
Tensile Strength, Yield 66.0 MPa
9570 psi
(50mm/min); ISO 527-2/1A
Aardvark Polymers AARTEL® 800 Rotational Molding Resin
Aartel 800 is our high test, general purpose, acetal copolymer. Aartel 800 provides overall excellent performance for most applications and is available in natural (off white) and a wide range of st..
Tensile Strength, Yield 66.0 MPa
9570 psi
SABIC - Japan Method
SABIC Innovative Plastics LNP LUBRICOMP Lexan_LF1000 PC (Asia Pacific)
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Shuman SP930 White Polycarbonate
Good impact strength, easy processability, good surface gloss, good heat resistance, excellent weatherability, excellent color stability, self-extinguishing.Data provided by the manufacturer.
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP KF002L Acetal Homopoly
LNP* THERMOCOMP* KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible.
Tensile Strength, Yield 66.0 MPa
9570 psi
SABIC - Japan Method
SABIC Innovative Plastics NORYL N300 PPE (Asia Pacific)
High Heat 150deg.C, FR V-0
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics Valox® SHF4910 PBT (Europe-Africa-Middle East)
6.5% glass reinforced, Super High Flow, flame retardant PBT.
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
SABIC Innovative Plastics Noryl 731H PPE+PS
High gloss, general purpose grade. 130C (266F) DTUL. UL 94 HB rated. For multiple plugs, wine filter plates, etc.This data was supplied by SABIC-IP for the Americas region.
Tensile Strength, Yield 66.0 MPa
9570 psi
ISO 527-1/-2
Covestro Bayblend® T95 MF* Polycarbonate + ABS, Mineral Filled
Developmental productInjection molding grade9 % mineral filledvery high heat resistancereduced coefficient of linear thermal expansiontensile modulus = 3350 MPaVicat/B 120 = 142 °CPreprocessingMax...
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527-1,-2
Covestro Makrolon® 2407 MAS145 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Low..
Tensile Strength, Yield 66.0 MPa
9570 psi
ISO 527-1/-2
Covestro Makrolon® 2558 Polycarbonate
ISO 7391-PC,MR,(,,)-18-9MVR (300 °C/1.2 kg) 14.5 cm3/10 minMedical devicessuitable for ETO and steam sterilization at 121 °CComplies with the requirements of FDA-modified ISO 10993-1 and USP Class..
Tensile Strength, Yield 66.0 MPa
9570 psi
ISO 527-1/-2
Covestro Makrolon® 2656 Polycarbonate
ISO 7391-PC,MR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minFood contact qualityMedium viscosityEasy releaseGood hydrolysis resistanceInjection molding - Melt temperature 280 - 320 °CAv..
Tensile Strength, Yield 66.0 MPa
9570 psi
ISO 527-1/-2
Covestro Makrolon® 2665 Polycarbonate, Flame Retardant Grade
ISO 7391-PC,MFR,(,,)-18-9Global gradeMVR (300 °C/1.2 kg) 12.5 cm3/10 minChlorine- and bromine-free flame retardantUL 94V-2/1.5 mm and 3.0 mmMedium viscosityEasy releaseInjection molding - Melt temp..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527-1,-2
Covestro Makrolon® 3107 MAS167 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• General purpose• Hig..
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527-1,-2
Covestro Makrolon® FU4007 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Furniture applications..
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Aclo Accutech Polypropylene CP0435G43CV Copolymer Glass Reinforced Coupled
Approved to GMP.PP.039 Black A13054
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Solvay Specialty Polymers Mindel® S-1000 Modified Polysulfone  (discontinued **)
This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.
Tensile Strength, Yield 66.0 MPa
9570 psi
ASTM D638
Ashley Polymers Ashlene® R6041 Nylon 66, PTFE and Silicone Modified
Nylon 66 PTFE and Silicone modified for excellent wear characteristics and low friction.Data provided by the manufacturer
Tensile Strength, Yield 66.0 MPa
9570 psi
50 mm/min; ISO 527
SABIC Innovative Plastics Noryl FXN2090H PPE+HIPS (Asia Pacific)
Noryl* FXN2090H resin is an unfilled, injection moldable grade. Designed for exceptionally high gloss and improved pencil hardness vs. standard Noryl grades, FXN2090H resin uses non-halogenated FR a..