SABIC Innovative Plastics NORYL PX9406 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL PX9406 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nonbrominated, nonchlorinated, flame retarded. Improved productivity and reliability. 252F HDT. UL94 V-0 rated. Electrical applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 18 % | 18 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 9.5 % | 9.5 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 111 MPa | 16100 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.64 GPa | 383 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.21 J/cm | 21.00 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 42.0 J | 31.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C @Thickness 6.40 mm |
271 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 6.40 mm |
252 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 150 °C | 302 °F | Rate B/50; ASTM D1525 |
| UL RTI, Electrical | 110 °C | 230 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.760 mm |
V-0 @Thickness 0.0299 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.49 @Frequency 1.00e+6 Hz |
2.49 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 2.57 @Frequency 50.0 - 60.0 Hz |
2.57 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 18.8 kV/mm @Thickness 3.20 mm |
478 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0026 @Frequency 1.00e+6 Hz |
0.0026 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.0052 @Frequency 50.0 - 60.0 Hz |
0.0052 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A |
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F2 | UL 746C |
Users viewing this material also viewed the following: