- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 252 °F
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 252 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 121R PC (Europe-Africa-Middle East) LEXAN 121R is a low viscosity multi purpose grade and contains a release agent to ensure easy processing. LEXAN 121R is available in transparent, translucent and opaque colours. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 915R PC (Europe-Africa-Middle East) Lexan* 915R Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has a UL V0 rating with good flow and mold release properties... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® EXL6033 PC (Europe-Africa-Middle East) PC-Siloxane copolymer with good processability.Very low temp. ductility, UV-Stabilized, UL94 V1 rated in white colors only.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® FXD123R PC (Europe-Africa-Middle East) LEXAN FXD123R is a transparent/translucent low viscosity grade for light diffusion special effects. UV-stabilized. Color package may affect performance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® FXM171R PC (Europe-Africa-Middle East) LEXAN FXM171R is a transparent/translucent high flow grade for special effects colors with a metallic-luster appearance. Color package may affect performance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® IR1810 PC (Europe-Africa-Middle East) IR1810 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® LI1911R PC (Europe-Africa-Middle East) Low-viscosity multi-purpose grade having low levels of ionics species. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® VR2020 PC UL rated HB as of 10/97. 200 series recommended when V-2 rating required. Nonhalogenated. 17.5 MFR, for small, intricate parts. UV stabilized. Internal mold release.This data was supplied by SABIC-.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® 221R PC (Europe-Africa-Middle East) LEXAN 221R is a low viscosity multi purpose grade and contains a release agent to ensure easy processing. This grade is UL94-V2 at 0.4 mm approved. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Lexan® ML3732 PC (Europe-Africa-Middle East) Lexan ML3732 is a low viscosity flame retardant grade, especially designed to pass the glow wire test according EDF HN60-S-02 at a thickness of 3.2 mm. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 - 254 °C | 252 - 490 °F | Average value: 143 °C Grade Count:109 |
| Overview of materials for Polycarbonate, 20% Glass Filled This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, 20% Glass Filled". Specific grades with glass content between 15% and 24% are included. E.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP DX98306H PC (Asia Pacific) LNP* Lubricomp* DX98306H is a compound based on Polycarbonate resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated, Low Extractible. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics PC2200 PC (Asia Pacific) PC2200 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics PC2200 PC (Europe-Africa-Middle East) PC2200 resin is a high flow (MFR = 22 at 300?C/1.2kg), heat stabilized, polycarbonate product designed for use in the custom compounding market. It does not contain UV stabilizer or mold release. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
ASTM D 648 |
| SABIC Innovative Plastics PC2200R PC PC2200R resin is a high flow (MFR = 22 at 300ºC/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was supplied by S.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
ASTM D 648 |
| SABIC Innovative Plastics PC2200R PC (Europe-Africa-Middle East) PC2200R resin is a high flow (MFR = 22 at 300ºC/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market.This data was supplied by S.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
ASTM D648 |
| SABIC Innovative Plastics PC2203R PC (Europe-Africa-Middle East) PC2203R resin is a high flow (MFR = 22 at 300?C/1.2kg), heat and UV stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| SABIC Innovative Plastics LNP Thermocomp DX93681 PC (Asia Pacific) LNP* Thermocomp* DX93681 is a compound based on Polycarbonate resin containing Proprietary Filler(s).This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 6.40 mm |
252 °F @Thickness 0.252 in |
ASTM D648 |
| Samsung Cheil Industries Infino® FD-1122 PC, FR Information provided by Samsung Cheil Industries. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 6.40 mm |
252 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL NH5020 PPE+PS (Europe-Africa-Middle East) Noryl* NH5020 Resin is an unreinforced blend of Polyphenylene Ether(PPE) + Polystyrenre resin. The material offers a good balance of heat, flow, hydrolytic stability, and non-halogenated flame reta.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Europe-Africa-Middle East) Noryl* NH6010B resin is a high performance, modified PPE-PS blend that exhibits an excellent balance of lower smoke production upon burning, nonhalogenated flame retardance and low specific gravity... |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL PKN4775 PPE+PS (Asia Pacific) PPE+PS blend. Opaque. FDA compliant in limited colors. High heat. Modulus at elevated temperature. Good ESCR performance. Thin wall extrusion and injection molding. Typical applications include pack.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP SH1100A PA12 LNP* Thermocomp* SH1100A is a Nylon 12, High Specificy Gravity compound containing proprietary fillers. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Post Baked; ASTM D648A |
| Sumitomo Bakelite North America E 16521A Electrical Encapsulation Grade Epoxy E-16521A is an encapsulation grade epoxy molding compound suitable for electrical applications such as coils.Information provided by Sumitomo Bak North America, Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C @Thickness 3.20 mm |
252 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL EXNL0143 PPE+PS Noryl PX1736 Resin is a blend of PPE and PS, that provides high strength, increased heat resistance, and translucency. The material has melt strenght suitable for Extrusion and Blow Molding applica.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | 0.25 inch; ASTM D648 |
| PlastxWorld CEVIAN® S1210 PC/ABS alloy Glass fiber reinforced PC/ABS alloy.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ISO 75-1/-2 |
| Covestro Makrolon® 1260 Polycarbonate, Impact Grade ISO 7391-PC,MPR,(,,)-24-9Global gradeMVR (300 °C/1.2 kg) 34 cm3/10 minImpact modifiedLow viscosityEasy releaseInjection molding - Melt temperature 280 - 320 °CAvailable in light colors onlyPreproc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | |
| Aclo Accucomp Polycarbonate POL051L Medium Viscosity |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | ASTM D648 |
| Ashley Polymers Ashlene® 1621 Polycarbonate A general purpose injection molding grade, natural resin, UL approved. Also available as: 1621R (with release); 1623 (with UV stabilizers); 1623R (with release and UV stabilizers).Data provided by .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Lexan® 123X PC Copolymer (Asia Pacific) Improved flow PC with excellent processability and mold release. |
|||