SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* RFL159 is a compound based on Nylon 66 resin containing 25% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant, Flame Retardant
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 |
| Density | 1.62 g/cc | 0.0585 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.320 % | 0.320 % | 50% RH, 24 hrs; ASTM D570 |
| 0.490 % | 0.490 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.030 cm/cm @Time 86400 sec |
0.0090 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 149 MPa | 21600 psi | 5 mm/min; ISO 527 |
| 153 MPa | 22200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 149 MPa | 21600 psi | 5 mm/min; ISO 527 |
| 153 MPa | 22200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.91 GPa | 1582 ksi | 1 mm/min; ISO 527 |
| 11.28 GPa | 1636 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| 215 MPa | 31200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 215 MPa | 31200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.51 GPa | 1380 ksi | 2 mm/min; ISO 178 |
| 9.70 GPa | 1410 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.790 J/cm | 1.48 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.39 J/cm | 13.8 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.42 | 0.42 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.47 | 0.47 | ASTM D3702 Modified |
| K (wear) Factor | 6.04 x 10-8 mm³/N-M | 3.00 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 72.5 x 10-8 mm³/N-M | 36.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 244 °C @Thickness 3.20 mm |
471 °F @Thickness 0.126 in |
unannealed; ASTM D648 |