- Polymer Property : Tensile Strength at Break = 7980 psi
Polymer Property : Tensile Strength at Break = 7980 psi Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Cycoloy® CE1821 PC+ABS (Europe-Africa-Middle East) High stiffness PC/ABS blend offering high impact, high heat, low CTE, good surface quality and excellent extrusion and thermoforming characteristics.This data was supplied by SABIC-IP for the Europe.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1112 PC Copolymer (Asia Pacific) Lexan* EXL1112 polycarbonate (PC) siloxane copolymer resin is a high flow opaque injection molding (IM) grade. This resin offers good low temperature (-20 C) ductility in combination with excellent .. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1132 PC Copolymer Lexan* EXL1132 polycarbonate (PC) siloxane copolymer resin is a high flow, UV stabilized injection molding grade. This resin offers good low temperature (-20 C) ductility in combination with high fl.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® EXL1464T PC Copolymer (Asia Pacific) Lexan* EXL1464T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers extreme low temperature (-40 °C) ductility in combination with medium flo.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Lexan® FXD951A PC Visual effetcs diffusion, flame retardant PC with low/medium flow good for extrusion/injection molding applications. Ideal for light management platforms that require hiding power and transmission.T.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics Lexan® LUX7430C PC COPOLYMER (Asia Pacific) Lexan* LUX7430C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating at 1.2 mm / 5VA rating at 3.0mm a.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Lexan® OQ1060 PC Copolymer Optical quality, high flow, high purity Polycarbonate copolymer resin with reduced oxygen transmission for advanced DVD applications such as Limited Play DVD.This data was supplied by SABIC-IP for t.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-1/-2 |
| DSM Akulon® K-FHGM24 (Cond.) 30% Glass/Mineral Reinforced, Nylon 6 (North America)
(discontinued **) Description: The Akulon portfolio is engineered for optimum performance to suit different processing techniques and end use markets.Unfilled Extrusion ResinsAkulon resins are available with melt vis.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 - 1/2 |
| Hexion Bakelite™ X22 Phenolic Formaldehyde Resin, UL Listed
(discontinued **) Phenolic molding compound, mainly organically filled, UL listed molding compound 3.0 mm/V-0 (BN, BK).Application areas: Pot handles, operating controls, electrical isolators, housing parts.Informati.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | cond.; ISO 527-1, -2; 5 mm/min |
| Lanxess Durethan® BKV 215 000000 Nylon 6-Copolymer, Glass Fiber Reinforced, Impact Modified PA 6-Copolymer, 15% glass fibers, injection molding impact modifiedInformation provided by LANXESS. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50mm/min; ASTM D638 |
| Kingfa LONOY 2100 LT PC/PET Alloy Features:Excellent balance propertiesGood weather resistanceGood size stabilitySmooth surfaceUniform colorApplications:Injection moldingAutomobile bumperAutomobile interior/exterior trim partsBusine.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Conditioned; ISO 527-1/-2 |
| Lanxess Durethan® BKV 315 Z H2.0 901510 Nylon 6, 15% Glass Fiber PA 6 extrusion- and blow molding-grade with 15% glass fibers, branched/structural viscosity, elastomer-modified, good heat-ageing resistance, dry-impact modifiedApplication Examples: air intake hose.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics NORYL V0150B PPE+HIPS Noryl* V0150B is an unfilled, injection moldable modified polyphenylene ether resin.. Designed for high heat resistance and thin wall FR performance, this resin delivers a UL94 V0 rating at 1.5 mm a.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific) LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP GL003 PSU (Asia Pacific) LNP* Lubricomp* GL003 is a compound based on Polysulfone resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC LNP* Lubricomp* Lexan_WR5210R compound is a wear resistant, 7% PTFE filled PC. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP PFP36 PA 6 (Asia Pacific) LNP* PFP36 is a compound based on Nylon 6 containing Glass Fiber and PTFE/Silicone. Characteristics are Impact Modifier. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP RP003 PA 66 LNP* LUBRICOMP* RP003 is a compound based on Nylon 66 resin containing 15% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics XYLEX X7300 PC+POLYESTER PC+POLYESTER unreinforced alloy. High flow, chemically resistant with excellent optical quality. UV-stabilized. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-1/-2 |
| Styrolution Polystyrol 158 K GR 2 PS Description: Polystyrol 158 K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blend s with high impact Polystyrol in heat contact applicati.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-1/-2 |
| Styrolution Polystyrol 158 K GR 21 PS Description: Polystyrol 158 K is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blend s with high impact Polystyrol in heat contact applicati.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| SABIC Innovative Plastics NORYL GTX GTX914 PPE+PA (Asia Pacific) NORYL GTX914 is an unfilled GTX grade with an ideal combination of impact performance, dimensional stability at elevated temperatures, chemical resistance and processability. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| SABIC Innovative Plastics Noryl PX1115 PPE+HIPS (Europe-Africa-Middle East) NORYL PX1115 is an unfilled, flame retardant material with a Vicat B/120 of 140°C according ISO 306. NORYL PX1115 is V1 at 1.2 mm according UL94 and halogen free according VDE/DIN 472 part 815.Th.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp XL004 Amorphous Polyamide LNP* Lubricomp* XL-4040 is a compound based on Amorphous Nylon, containing PTFE.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics Xenoy® X4810 PBT+PC (Asia Pacific) Xenoy X4810 is a hydrostable, High Modulus Ductile PC/PBT blend. This resin provides low temperature (below 0C) ductile impact behaviour, high chemical resistance, very low creep, low CTE, excellent.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ISO 527-93 |
| Wellman Wellamid® FR22F-NBK3 Flame Retardant Nylon 66 Description: Flame Retardant Nylon 66Information provided by Wellman. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® BS/2 PA6 Product description: Grilon BS/2 is an unreinforced, nucleated standard PA6 injection molding grade with normal melt viscosity. Grilon BS/2 has the following important properties: Good flow behavior.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | conditioned; ISO 527-1/-2 |
| EMS-Grivory Grivory® EBGM-20 HX PA666-GF15 Product description: Grilon EBGM-20 HX black 9992 is a high viscosity, high heat stabilized PA66 + PA6 extrusion blow molding grade with 15% glass fibers. The special features of Grilon EBGM-20 HX b.. |
|||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | ASTM D638 |
| Arkema Group Pebax® 6333 Polyether Block Amide (PEBA) Information provided by Arkema Group |
|||