SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR

Category Polymer , Thermoplastic , Polyurethane, TP
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity.
Physical Properties Metric English Comments
Density 6.03 g/cc
0.218 lb/in³
ISO 1183
6.046 g/cc
0.2184 lb/in³
ASTM D792
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
0.180 %
0.180 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0096 cm/cm

@Time 86400 sec
0.0096 in/in

@Time 24.0 hour
ISO 294
0.010 cm/cm

@Time 86400 sec
0.010 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0076 cm/cm

@Time 86400 sec
0.0076 in/in

@Time 24.0 hour
ISO 294
0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 14.0 MPa
2030 psi
ISO 527
17.0 MPa
2470 psi
ASTM D638
Tensile Strength, Yield 17.0 MPa
2470 psi
ISO 527
19.0 MPa
2760 psi
ASTM D638
Elongation at Break 25.8 %
25.8 %
ASTM D638
52.1 %
52.1 %
ISO 527
Elongation at Yield 11.3 %
11.3 %
ISO 527
14.4 %
14.4 %
ASTM D638
Tensile Modulus 0.920 GPa
133 ksi
1 mm/min; ISO 527
1.10 GPa
160 ksi
50 mm/min; ASTM D638
Flexural Strength 18.0 MPa
2610 psi
ISO 178
22.0 MPa
3190 psi
ASTM D790
Flexural Modulus 0.960 GPa
139 ksi
ISO 178
0.980 GPa
142 ksi
ASTM D790
Izod Impact, Notched 2.99 J/cm
5.60 ft-lb/in
ASTM D256
Izod Impact, Unnotched 13.67 J/cm
25.61 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 18.0 kJ/m²
8.57 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 85.0 kJ/m²
40.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 16.0 J
11.8 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 12.0 J
8.85 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 88.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
49.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
88.9 µm/m-°C

@Temperature -40.0 - 40.0 °C
49.4 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 75.0 °C
167 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
71.0 °C

@Thickness 3.20 mm
160 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 45.0 °C
113 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
44.0 °C

@Thickness 3.20 mm
111 °F

@Thickness 0.126 in
unannealed; ASTM D648