Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | |
Eastman Eastar GN101 PETG Copolyester
(discontinued **) ISO data as provided by the manufacturer, Eastman Chemical |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
ExxonMobil HD 6908.18 Injection Molding Resin
(discontinued **) HD 6908 is a homopolymer with outstanding stiffness with a good balance of processability and cold temperature impact performance. This resin is ideally suited for articles requiring very high stif.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Fiberfil® PP-61/VO/NH Polypropylene Copolymer, Flame Retardant, non-halogenated, UL94 V0 Information provided by FIBERFIL Engineered Plastics |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Global PPC-0320 Standard Grade Polypropylene Information provided by Global Polymers Corporation. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Ineos HP53-25-155 HDPE HP53-25-155 is a high performance, high density polyethylene copolymer developed for blow molding. It is recommended for use in continuous extrusion blow molding equipment, specifically where appli.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | Unannealed; ISO 75B-1, -2 |
LyondellBasell Hifaxâ„¢ CB272 Thermoplastic Polyolefin Elastomer Description: Hifaxâ„¢ CB272 high melt flow, 900 MPa flexural modulus, low CLTE, paintable, mineral-filled thermoplastic elastomeric olefin (TEO) resin has a very good balance of rigidity and dime.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Spartech Marballoy Marbleized Thermoplastic Alloy Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Spartech Polylite Foamed Polyolefin Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Spartech PP7210 Calcium Carbonate Filled High Impact Copolymer Provides the highest level of impact of all copolymers and are useful in applications where improved processing and stiffness are required versus unfilled copolymer materials.Information provided by.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Spartech Soft Touch HDPE Polyolefin Skin/Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Spartech SP-1510 Polyolefin Sheet Description: Polyolefin SheetInformation provided by Spartech. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | ASTM D648 |
Spartech Ultros SRP Co-Extruded Skid-Resistant PE Specialty Sheet Description: Specialty SheetInformation provided by Spartech. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ISO 75-2 |
Borealis MG7547B Polyethylene MG7547B is a high-density polyethylene produced by a low pressure process. This grade has an excellent impact strength and low distortion even at low temperatures. It also contains UV stabilizer, wh.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ISO 75-2 |
Borealis MG7547S Polyethylene MG7547S is a high-density polyethylene produced by a low pressure process. This grade has an excellent impact strength and low distortion even at low temperatures. It also contains UV stabilizer, wh.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | Unannealed; ASTM D648 |
Lubrizol Isoplast® 101 Engineering Thermoplastic Polyurethane Resin ISOPLAST® 101 is an engineering thermoplastic polyurethane resin.Available in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Isoplast product li.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Eastman Cadence™ GS2 Copolyester for film calendering Eastman Cadence™ copolyester, for calendered films, is a specialty plastic developed to meet the demand for an environmentally responsible material for the calendering industry. Available in diffe.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Eastman Eastar CN005 Copolyester, High Flow Grade Applications:CompactsCosmetic jar capsCosmetic jarsCosmetics/personal care packagingFragrance capsFragrance packagingLip gloss containersLipstick containersPersonal care bottlesKey Attributes:Abilit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Eastman Eastar CN015 Copolyester, High Flow Grade with Mold Release Applications:CompactsCosmetic jar capsCosmetic jarsCosmetics/personal care packagingFragrance capsFragrance packagingLip gloss containersLipstick containersPersonal care bottlesKey Attributes:Abilit.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Eastman Eastar EN063 Polyester Eastar Polyester EN063 is a condensation polymer produced by a continuous melt-phase polymerization process followed by a solid-state polymerization process. Eastar Polyester EN063 is a homopolymer .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.1 °C | 160 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
Dow DMDA-8940 NT 7 High Density Polyethylene Resin DOW DMDA-8940 NT 7 is produced using UNIPOL™ process technology. It is intended for use in a broad range of injection molding applications such as housewares, toys, food containers and pails. Info.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | Unannealed; ASTM Data |
Dow Prevail® 3100 ABS + Polyurethane PREVAIL® 3100 thermoplastic resin offers designers and manufacturers a combination of flexibility and low temperature toughness not previously available in an engineering thermoplastic and is used .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
Braskem GP100BK HDPE High Density Extrusion Polyethylene GP100BK is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for water distribution. It is produced with bimodal technology and has high molar mass. It.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
Braskem GP5550 HDPE High Density Extrusion Polyethylene GP5550 is a high-density polyethylene with high molar mass. It is produced with bimodal technology and shows excellent mechanical properties and high resistance to stress cracking. Its applications .. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
Braskem GP5550BK HDPE High Density Extrusion Polyethylene GP5550BK is a high-density polyethylene with high molar mass. It is produced with bimodal technology and shows excellent mechanical properties and high resistance to stress cracking. GP5550BK contai.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Braskem JV 060U HDPE Injection Molding Polyethylene Applications: Caps, crates for industrial, transportation or fishing uses, industrial pails, stands and pallets, refuse containers; bottle cases, safety helmets, cages for poultry transportation and.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
Braskem IG58 HDPE Injection Molding Polyethylene Copolymer IG58 is a high-density polyethylene, narrow molecular weight butene-1 copolymer produced by the solution process for injection molding applications. It offers high stiffness, impact strength and out.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Braskem JV060U Injection Molding High Density Polyethylene Boxes for beverages bottles; Boxes in general; Technical parts.Information provided by Braskem. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ISO 75-2 |
Borealis MG9601 Polyethylene MG9601 is a natural high-density polyethylene with high melt-index and narrow molecular weight distribution, which is produced in a low-pressure gas-phase process. The grade is characterized by exce.. |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
Ineos HP50-25-153 HDPE A high performance, high density polyethylene copolymer developed for blow molding. It is recommended for use in applications which requiring excellent environmental stress crack resistance (ESCR)... |
|||
Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM-D648 |
Braskem BS600 HDPE Blow Molding Polyethylene Copolymer BS600 resin is a high-density polyethylene (HDPE), bimodal copolymer offering an outstanding combination of impact resistance and environmental stress crack resistance (ESCR). It is thus recommended.. |