Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 17.0 MPa | 2470 psi | STN EN ISO 527-2 |
Plastcom PLASTALEN® EQ 18 N Polyethylene Impact modified PE for extrusion. Delivered in black color.Information Provided by Plastcom spol. s r.o. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527 |
Polimeri Europa Eraclene® MP 90 High Density Polyethylene - Injection Molding Eraclene MP 90 is a high density polyethylene homopolymer resin (HDPE) with antioxidants, suitable for injection molding application.Eraclene MP 90 has a narrow molecular weight distribution and a h.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
Petroquimica Triunfo Trithene® TX 7003 LDPE - Heavy Duty and Industrial Film The Trithene® TX 7003 resin is a low-density, high molecular-weight polyethylene that offers high mechanical strength and environmental stress cracking resistance (ESCR). Additionally, this product.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
Ineos Styrenics Avantra® 594E High Impact Styrenic Polymer (NAFTA) Description: Avantra® 594E is a super high-impact polystyrene grade that delivers excellent processing efficiency along with toughness and high gloss in a wide variety of injection molding applic.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | UL 1581 |
SABIC Innovative Plastics NORYL WCD835 PPE-TPE Flexible, low odor, halogen free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame performance capable of meeting UL VW1 requirements. 80C end.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | 5 mm/min; ISO 527 |
SABIC Innovative Plastics LNP STAT-KON CD000I PS LNP* Stat-kon* CD000I is a compound based on Polystyrene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527 |
SABIC Innovative Plastics LNP STAT-KON MD000ISC PP (Asia Pacific) LNP STAT-KON* MD000ISC is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive. |
|||
Tensile Strength at Break | >= 17.0 MPa | >= 2470 psi | |
Sibur Neva Polyvinyl Chloride (PVC) Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a p.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
SABIC Innovative Plastics LNP THERMOCOMP TH0600A PUR (Asia Pacific) LNP THERMOCOMP* TH0600A is a compound based on Polyurethane resin. Added features of this material include: High Specific Gravity. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527 |
SABIC Innovative Plastics LNP THERMOCOMP TH0815A PUR (Asia Pacific) LNP* THERMOCOMP* TH0815A is a compound based on Polyurethane resin containing High Specific Gravity Filler. Added features of this material include: High Specific Gravity. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | 50 mm/min; ISO 527 |
SABIC Innovative Plastics NORYL WCD841U PPE-TPE Flexible, UV stabilized, halogen free extrusion grade for applications such as wire insulation and cable jacket. Good color stability after UV weathering per ASTM D4459. Light color capable. Flame r.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | Type I, 50 mm/min; ASTM D638 |
SABIC Innovative Plastics NORYL WCD851 PPE-TPE (Asia Pacific) Flexible, strong flame-retardant, halogen-free extrusion grade intended for evaluation in applications such as wire insulation and cable jacket. Flame retardant performance capable of meeting UL VW-.. |
|||
Tensile Strength at Break | >= 17.0 MPa | >= 2470 psi | 250mm/min; ISO 527 |
Borealis SuperCOPO™ LH4201R Polyethylene Insulation Compound, Crosslinkable SuperCOPO™ LH4201R is a crosslinkable natural polyethylene compound, specially designed for insulation applications. Applications: SuperCOPO™ LH4201R is intended for insulation of XLPE power cabl.. |
|||
Tensile Strength at Break | >= 17.0 MPa | >= 2470 psi | 250mm/min; ISO 527 |
Borealis Supercure™ LS4201R Polyethylene Insulation Compound, Crosslinkable Supercure™ LS4201R is a crosslinkable natural polyethylene compound, specially designed for insulation applications. Applications: Supercure™ LS4201R is intended for insulation of XLPE power cabl.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527-2/50 |
ExxonMobil Exxtral™ CMU 236 Performance Polyolefin Product Description: A specialty thermoplastic polyolefin resin designed for automotive interior covered applications such as retainers in which a good stiffness/toughness balance is required.Availa.. |
|||
Tensile Strength at Break | >= 17.0 MPa | >= 2470 psi | ISO R 527 |
Fainplast Compounds FR 83/1 Flexible PVC, Insulation General purposes |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO R 527 |
Fainplast Compounds MPH 78 Medical Flexible PVC, Extrusion Tubolar apparatus |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO R 527 |
Fainplast Compounds PH 70/AS Flexible PVC, Transparent Extrusion Food belt carriers |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO R 527 |
Fainplast Compounds PH 75 Flexible PVC, Transparent Extrusion Transparent profiles and pipes |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO R 527 |
Fainplast Compounds PHA 78 Flexible PVC, Transparent Extrusion Atoxic pipes |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO R 527 |
Fainplast Compounds PK 91 Flexible PVC, Lead Free Fencing |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D3759 |
3M 31U72C (Clear) Polyethylene Protective UV Tape 3M™ Protective UV Tape 31U72C is a 3 mil clear polyethylene self-wound film coated with a medium-high tack adhesive system featuring UV resistance.Information provided by 3M |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0336C20L Calcium Reinforced |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ASTM D638 |
Aclo Accutech Polypropylene Homopolymer HP0339C20L Calcium Reinforced |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | |
Plastcom SLOVALEN PQ 83 T 40 PP, 40% mineral filling FeaturesModified PP for injection moulding with the content of 40% mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased .. |
|||
Tensile Strength at Break | 17.0 - 34.0 MPa | 2470 - 4930 psi | ASTM D638 |
Arkema Group KYNAR FLEX® 2800-20 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Flexible. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical strength, low.. |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO R 527 |
Fainplast Compounds PM 92 Flexible PVC, Extrusion Semirigid profiles |
|||
Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527 |
SABIC Innovative Plastics LNP Stat-kon MD000IU PP LNP* Stat-kon* MD000IU is a compound based on Polypropylene resin containing Carbon Powder. Added features of this material include: Electrically Conductive, High Impact, UV Stabilized.This data wa.. |