- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 495 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 495 °F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.18 mm |
495 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| PolyOne LubriOne™ NN-30GF/13T-2S Black Polyamide 66 (Nylon 66) LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM UH1026 TPI Blend High heat amorphous TPI Blend, Chemical Resistant, High Flow, IR-Transparent |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM XH2315 TPI Resin Extem XH2315 Resin |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics EXTEM XH2315 TPI Resin (Asia Pacific) Extem XH2315 Resin |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ISO data |
| BASF Capron® GR630 30% Glass-Filled Nylon 66 (Dry)
(discontinued **) Capron GR630 is a 30% glass fiber reinforced polyamide 6,6 injection molding compound offering excellent strength, stiffness, creep resistance and dimensional stability. This balance of engineering.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.18 mm |
495 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GF 1200 A 43 Natural Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.18 mm |
495 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| PolyOne Nymax™ GF 1200 A 55 HS Black 13 Polyamide 66 (Nylon 66) The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durabil.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM D648 |
| Polymer Resources NY66-G33-[color]-H Nylon 66, 33% Glass Reinforced, Heat Stabilized Nylon 66, 33% Glass Reinforced, Heat Stabilized, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 6.40 mm |
495 °F @Thickness 0.252 in |
ASTM D648 |
| Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RFI12 PA 66 LNP* LUBRICOMP* RFI12 is a compound based on Nylon 66 resin containing 10% Glass Fiber, 2% Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RFL159 PA 66 LNP* LUBRICOMP* RFL159 is a compound based on Nylon 66 resin containing 25% Glass Fiber, 5% PTFE. Added features of this material include: Wear Resistant, Flame Retardant |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP RFN169 PA 66 LNP* LUBRICOMP* RFN169 is a compound based on Nylon 66 containing 30% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant, Flame Retardant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6 LNP* LUBRICOMP* RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RFP38 PA6.6 LNP* LUBRICOMP* RFP38 is a compound based on Nylon 66 containing 40% Glass Fiber, 15% PTFE/Silicone. Added feature of this grade is: Wear Resistant. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES HiFill® PA6/6 GF/M36 HS BK 36% Glass/Mineral Fiber Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 36% Filler by Weight and Mineral Filler, 36% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP STAT-KON RFD04 PA 66 LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM D648 |
| Techmer ES Plaslube® J-1/30/TF/10 Nylon 66, 30% GFR, 10% PTFE Plaslube glass fiber reinforced, polytetrafluoroethylene (PTFE) lubricated nylon 66 grades offer an excellent balance of wear and friction performance and mechanical strength. The addition of silic.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP THERMOCOMP RF006XXY PA 66 LNP* Thermocomp* RF006XXY is a compound based on Nylon 66 containing 30% Glass Fiber. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP THERMOCOMP RFB66 PA 66 LNP* THERMOCOMP* RFB66 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 30% Glass Bead. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP Thermocomp RFB24 PA 66 (Europe-Africa-Middle East) LNP* THERMOCOMP* RFB24 is a compound based on PA 66 resin containing Glass Bead, Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP VERTON RV00AESC PA 66 (Europe-Africa-Middle East) LNP* VERTON* RV00AESC is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding, Heat Stabilized. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM D648 |
| Plastics Group Polifil® 78MRGF Glass Fiber and Mineral Reinforced Nylon 6/6 (DAM) Polifil® GFN/MRN 6/6 reinforced series of compounds offer superior strength, rigidity and creep resistance. Glass fibers provide excellent thermal and dimensional stability while maintaining good h.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 120x10x4, sp=64 mm; ISO 75/Bf |
| Eurostar Staramide RFB24 PA66, 20/10% Glass Fiber/Glass Bead Filled Injection Molded RFB24 is a Glass Bead and Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as Staramide 66 2010VK Z3)Information provided by Polymer Technology & Services, the North American.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM D648 |
| Clariant Renol 6608G43 Nylon 66, 43% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM Test |
| BASF Ultramid® 1403-2 BK ND3007 PA66 (Dry) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM Test |
| BASF Ultramid® 1403-2 NF3001 13% Glass Filled PA66 (Dry) Ultramid 1403-2 NF3001 is a 13% glass reinforced, heat stabilized injection molding PA6/6. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | ASTM D648 |
| Ashley Polymers Ashlene® 527LD-45LG Nylon 66, 45% Long Glass Fiber Reinforced Long glass fiber reinforced impact modified Nylon 66, designed for parts requiring excellent thermal and dimensional stability and higher strength than available with conventional glass reinforced r.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Unannealed; ASTM D648 |
| Techmer ES Statiblend® PPS GF35 SS7 BK 35/7% Glass/Stainless Steel Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass/Stainless Steel Fiber, 35/7% Filler by WeightUL File Number: E157318Appearance: BlackInformation provided by TP Composites, Inc. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL APS440 PPE+PPS (Asia Pacific) |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| SABIC Innovative Plastics LNP VERTON RX00327 PA 66 LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural. |
|||