- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 254 °C
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 254 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Polymer Resources NY66-M25G15 Nylon 66, 25% Mineral, 15% Glass Reinforced Nylon 66, 25% Mineral, 15% Glass Reinforced, LubricatedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon gr.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Polymer Resources NY66-M25G15-[color]-H Nylon 66, 25% Mineral, 15% Glass Reinforced, Heat Stabilized Nylon 66, 25% Mineral, 15% Glass Reinforced, Lubricated and Heat StabilizedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, te.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | DAM; ISO 75-1/-2 |
| DuPont Performance Polymers Zytel® HTN 53G50HSLR BK083 Polyphthalamide (PPA)
(Unverified Data**) Zytel® HTN53G50HSLR BK083 is a 50% glass reinforced, heat stabilized, lubricated high performance polyamide resin developed for moderate temperature structural applications requiring retention of h.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP RCP36 PA 66 (Asia Pacific) LNP LUBRICOMP* RCP36 is a compound based on Nylon 66 resin containing Silicone, PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF30 IM HS L 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF30 IM2 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF43 IM L 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 43% Filler by WeightAdditive: Lubricant and Impact ModifierFeatures: Lubricant and Impact ModifiedTPCI# 6439.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF20 TL15 BK 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 20% Filler by WeightAdditive: PTFE Lubricant(15%) Features: Lubricated, Good Wear Resistance and Low Friction Appearance:.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF20 TS15 BK 20% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 20% Filler by WeightAdditive: PTFE Lubricant(10%) and Silicone Lubricant Features: Lubricated, Good Wear Resistance and L.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF30 TL12 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%) and Silicone LubricantFeatures: Lubricated, Good Wear Resistance and Lo.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 CF30 TS15 BK 30% Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber, 30% Filler by WeightAdditive: PTFE Lubricant(15%) and Silicone LubricantFeatures: Lubricated, Low Friction and Good Wear .. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF30 ML5 HS BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Molybdenum Disulfide Lubricant(5%)Features: Lubricated and He.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Luriblend® PA6/6 GF30 X 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated, Good Wear Resistance, Low Friction and He.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C @Thickness 6.40 mm |
489 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics NORYL GTX GTX830 PPE+PS+PA (Asia Pacific) GR 30%. Highest stiffness of 1200000 psi (8200 MPa) flexural modulus. Excellent chemical and high heat resistance. Application: under the bonnet. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF30 IM2 UV 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 30% Filler by WeightAdditive: UV Stabilizer, Heat Stabilizer, Lubricant and Impact ModifierFeatures: Good UV.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF33 IM HS L BK 33% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 33% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Techmer ES Elastoblend® PA6/6 GF43 IM HS L 43% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 43% Filler by WeightAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Heat Stabilized, Lubri.. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Chase Plastics CP Pryme® NN113GL (DAM) Nylon 66, 13% Glass Fiber Reinforced, Internally Lubricated Information provided by Chase Plastics. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MK4015 40% Glass Fiber/Mineral Reinforced 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MK4015H 40% Glass Fiber/Mineral Reinforced, Heat Stabilized Nylon 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MK4015 40% Glass Fiber/Mineral Reinforced 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MK4015 40% Glass Fiber/Mineral Reinforced 66 Information provided by A. Schulman. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Clariant Renol 6608G33HSL Nylon 66, 33% Glass Fiber, Impact Modified, Heat Stabilized, Lubricated Data provided by Clariant Masterbatches |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| Ashley Polymers Ashlene® 528L-40G Nylon 66, 40% Glass Reinforced A general purpose 40% glass reinforced Nylon 66 resin.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| Ashley Polymers Ashlene® 528L-43G Nylon 66, 43% Glass Reinforced A general purpose 43% glass reinforced nylon resin.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| Ashley Polymers Ashlene® 528L-50G Nylon 66, 50% Glass Reinforced A general purpose 50% glass reinforced Nylon 66 resin.Data provided by the manufacturer |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 757 Carbon Fiber Reinforced, Flow Enhanced, PPS Alloy Data provided by the manufacturer, ComAlloy International Company.30% Carbon Fiber Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 489 °F | ASTM D648 |
| A. Schulman SCHULAMID® 66 MK4015 40% Glass Fiber/Mineral Reinforced 66 Information provided by A. Schulman. |
|||